Structure, nanohardness and photoluminescence of ZnO ceramics based on nanopowders
ZnO ceramics obtained from grained powders with different grain size by hot pressing and ceramics from tetrapods nanopowders obtained by press-less sintering have been investigated under identical conditions. Ceramics obtained by hot pressing were optically transparent but were composed of large inhomogeneous grains (d = 8–35 μm) exhibiting a substructure. Decreased values of elastic modulus within a grain and a wide defect-associated ('green') photoluminescence (PL) band at 2.2–2.8 eV in conjunction with a weak excitonic band indicate a high concentration of residual point defects in hot pressed ZnO ceramics. Utilization of more small-grained powders contributes to the formation of more un…
Ultrafast luminescence of Ga- and In-doped ZnO ceramics
The work of authors (a-c) was financially supported by Russian Foundation for Basic Research (RFBR, Russia) and the work of the last author (d) had financial support from State Education Development Agency (VIAA, Latvia) . All of that was approved as a result of ERA.Net RUS PLUS 2017 joint call for proposals. Here is the link for the joint call for reference: https://www.eranet-rus.eu/en/196.php .
ZnO and ZnO:Ga Ceramics for Advanced Scintillators
The undoped ZnO reveals narrow luminescence bands located close to fundamental absorption edge, known as near band luminescence (NBL) and defects related wide luminescence band within visible range of spectrum. NBL decay is in sub-nanosecond range and it is promising for fast scintillator development. However, the defects luminescence decay is in microsecond range and it is disturbing for fast scintillators. Dopants strongly change the luminescence properties, mainly the intensity and decay time and that is the cause for intense study of doped ZnO luminescence properties. Thus the study of luminescent properties of undoped ZnO and doped ZnO:Ga ceramics was carried out. The dependence of the…
Sub-nanosecond excitonic luminescence in ZnO:In nanocrystals
The financial support of research European Union ERA.NET RUS_ST20170-51 . This work was partly supported by Russian Foundation for Basic Research, Russia , project No. 18-52-76002 . The sample preparation was carried out as part of SFERA II project -Transnational Access activities ( European Union 7th Framework Programme Grant Agreement N3126430 ).
Effect of in Doping on the ZnO Powders Morphology and Microstructure Evolution of ZnO:In Ceramics as a Material for Scintillators
Transparent ZnO ceramics are of interest for use as material for high-efficiency fast scintillators. Doping ZnO ceramics in order to improve complex of their properties is a promising direction. In the present research, the role of indium in the ZnO nanopowders surface interactions and in the change of microstructures and photoluminescence (PL) characteristics of sintered cera-mics is considered. Undoped and 0.13 wt% In doped ZnO ceramics are obtained by hot pressing sintering. It has been found that indium leads to the transition of initially faceted ZnO particles to rounded, contributing to good sintering with formation of diffusion active grain boundaries (GBs). Unlike ZnO ceramics, ZnO:…