Uptake of actinides by calcium silicate hydrate (C-S-H) phases
Abstract The sorption of actinides (Th, U – Am) was studied in dependence of the solid-to-liquid (S/L) ratio (0.5–20.0 g/L) and the calcium-to-silicon (C:S) ratio. The C:S ratio was varied between 1.80 and 0.70 to simulate the changing composition of the C-S-H phases during cement degradation from high to low C:S ratios. The decrease of the calcium content in the C-S-H phases by time is accompanied by a decrease in pH in the corresponding suspensions from 12.6 to 10.2. X-ray photoelectron spectroscopy (XPS) of the C-S-H phases showed an increasing depletion of Ca on the surface with increasing C:S ratio in comparison to the composition of the solid phase as a whole. The sorption experiments…
Investigation of the Electrophoretic Mobility of the Actinides Th, U, Np, Pu, and Am in Different Oxidation States.
The electrophoretic mobilities (μe) of the actinides Th and U-Am in different oxidation states (prepared in 1 M HCl and 1 M HClO4) have been determined by capillary electrophoresis (CE)-inductively coupled plasma mass spectrometry (ICPMS) using 1 M acetic acid as the background electrolyte, which has proven to provide an excellent setup for trace analysis at environmentally relevant concentrations (1 × 10-9 M). The values are independent of the respective acid solution. The μe of the Pu oxidation states +III to +VI have been measured. They agree with both the available literature data and the redox-stable analogues (Eu(III), Th(IV), Np(V), U(VI)) that have also been investigated. The trend …