Preparation and photoactivity of nanocrystalline TiO2 powders obtained by thermohydrolysis of TiOSO4
2013
Nanocrystalline TiO2 photocatalysts were synthesized in mild conditions by thermohydrolysis of TiOSO4 in water at 100 °C and post-calcination treatment at various temperatures. The TiO2 powders were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, specific surface area determinations, scanning electron microscopy and electron paramagnetic resonance measurements. The photoactivity of the samples was tested employing the photodegradation of 4-nitrophenol in liquid–solid regimen and the photooxidation of gaseous 2-propanol. The best results were obtained with the powder calcined at 600 °C for 10 h. Surprisingly, the not calcined sample was the most active for the abatement…
N-TiO2 Photocatalysts highly active under visible irradiation for NOX abatement and 2-propanol oxidation
2013
N-doped TiO2 powders were prepared by two different sol-gel methods. Samples were characterised by X-ray diffraction (XRD), BET specific surface area measurements (SSA), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS) and Electron Paramagnetic Resonance (EPR). XPS measurements revealed a signal at 400 eV assignable to nitrogen in the form of Ti-N-O. EPR signals are attributed to molecular NO trapped with cavities/defects possibly interacting with oxygen vacancies. The photocatalytic activity under UV and visible light was determined following the abatement of NOx and the photodegradation of 2-propanol in gas-solid systems. N…