Evaluation and Comparison of Novel Precursors for Atomic Layer Deposition of Nb2O5 Thin Films
Atomic layer deposition (ALD) of Nb2O5 thin films was studied using three novel precursors, namely, tBuN═Nb(NEt2)3, tBuN═Nb(NMeEt)3, and tamylN═Nb(OtBu)3. These precursors are liquid at room temperature, present good volatility, and are reactive toward both water and ozone as the oxygen sources. The deposition temperature was varied from 150 to 375 °C. ALD-type saturative growth modes were confirmed at 275 °C for tBuN═Nb(NEt2)3 and tBuN═Nb(NMeEt)3 together with both oxygen sources. Constant growth rate was observed between a temperature regions of 150 and 325 °C. By contrast, amylN═Nb(OtBu)3 exhibited limited thermal stability and thus a saturative growth mode was not achieved. All films we…
Plasma-Enhanced Atomic Layer Deposition of Silver Thin Films
Thermal properties of various silver precursors known in the literature were evaluated in order to discover which precursor is the most suitable one for plasma-enhanced atomic layer deposition (PEALD) of silver thin films. Ag(fod)(PEt3) (fod = 2,2-dimethyl-6,6,7,7,8,8,8-heptafluorooctane-3,5-dionato) was found to be the best choice. Using Ag(fod)(PEt3) together with plasma-activated hydrogen, silver thin films were deposited at growth temperatures of 120–150 °C, and ALD-type saturative growth was achieved at 120–140 °C. At 120 °C, the growth rate was 0.03 nm per cycle. The plasma exposure time had also an effect on the growth rate: with shorter exposure times, the growth rate was lower over…