Evidence of nickel ions dimerization in NiWO4 and NiWO4-ZnWO4 solid solutions probed by EXAFS spectroscopy and reverse Monte Carlo simulations
2021
Abstract The existence of exchange-coupled Ni 2 + ions – the so-called magnetic dimers – in wolframite-type NiWO 4 and Zn c Ni 1 − c WO 4 solid solutions with high nickel content was discovered by X-ray absorption spectroscopy combined with reverse Monte Carlo (RMC) simulations. Temperature- (10–300 K) and composition-dependent X-ray absorption spectra were measured at the Ni K-edge, Zn K-edge, and W L 3 -edge of microcrystalline NiWO 4 , Zn c Ni 1 − c WO 4 and ZnWO 4 . Structural models were obtained from simultaneous analysis of the extended X-ray absorption fine structure (EXAFS) spectra at three metal absorption edges using RMC simulations. The obtained radial distribution functions for…
Influence of mechanoactivation on the adhesion and mechanical properties of metal/oxide interfaces
2005
Properties of interfaces in solid state metal/oxide joints (Al/SiO2, Al/MgO, Al/glass, Mg/MgO, In/glass, Mg/SiO2 etc.) are reported. Interfaces were formed at plastic deformation of metal on the oxide surface at room temperature. Structure, composition, and micromechanical properties of the interfaces are studied by AFM, X-ray diffraction, SIMS, electron, optical microscopy, and precision microindentation. A noticeable adhesion is observed in the regions of maximum shear strain in case of metals with low oxide formation energy. Formation of a reaction zone with oxygen concentration gradient is detected in which the metal near the interface hardens. The effect of mechanoactivation is conside…
Chemical-state analyses of Ni, Zn, and W ions in NiWO$_4$-ZnWO$_4$ solid solutions by X-ray photoelectron spectroscopy
2022
The chemical states of Ni, Zn, and W in microcrystalline NiWO$_4$-ZnWO$_4$ solid solutions were studied by X-ray photoelectron spectroscopy. The recorded spectra of the Ni 2p, Zn 2p, and W 4f photoelectron lines and Ni L$_2$M$_{23}$M$_{45}$, Zn L$_3$M$_{45}$M$_{45}$, and W N$_4$N$_{67}$N$_{7}$ Auger-transition lines show pronounced changes with increasing Zn concentration. The positions of the resolved photoelectron and Auger-transition lines were combined to construct so-called chemical-state plots (Wagner or Auger-parameter plots) for metal ions in solid solutions. With increasing Zn concentration, the Auger parameter increases for Ni and decreases for W, thus evidencing a lowering and an…
Nanostructured metal/oxide coatings
2007
Al based nanocomposite coatings on Cu and glass substrates were obtained in the conditions of severe shear stresses by deformation scheme similar to that of friction. Structure, composition and micromechanical properties were investigated using AFM, XRD, SIMS, electron, optical microscopy and precision microindentation techniques. Coatings are characterized by the high microhardness and good adhesion to the substrates. This is determined by the formation of nanostructured Al-oxide composite stabilized by the presence of oxidized interlayers, which are barriers for the grain growth and intermetallic phase formation. The annealing in vacuum leads to the development of oxygen redistribution pr…
X-ray absorption and Raman spectroscopy studies of tungstates solid solutions ZncNi1-cWO4 (c=0.0-1.0)
2020
G.B. acknowledges the financial support provided by the State Education Development Agency for project No. 1.1.1.2/VIAA/3/19/444 (agreement No. 1.1.1.2/16/I/001) realized at the Institute of Solid State Physics, University of Latvia. A.K. and A.K. would like to thank the support of the Latvian Council of Science project No. lzp-2019/1-0071. Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART2.
Obtaining of nanostructured ZnO coatings using mechanoactivated oxidation
2007
The concept to use nanostructured state of metal at the instant of destruction in air environment was used to obtain nanostructured Zn-ZnO coatings on glass and quartz by mechanical method. Subsequent annealing in the ambient atmosphere, annealing in vacuum and irradiation with 532-nm YAG:Nd laser were used to obtain completely oxidized, transparent ZnO coatings. The saturated with oxygen nanostructured coatings were transformed into nanostructured ZnO coatings after annealing above 773K or irradiation with laser (allowing to reach 673K) in ambient atmosphere. AFM and SEM images show that after annealing ZnO coatings have multi-shaped structure. The formation of ZnO need-like whiskers (d = …
Adhesion and interfacial reactions on metal/oxide interface during plastic deformation at room temperature
2005
Properties of interfaces in solid state metal/oxide joints (Al/SiO2, Al/MgO, Al/glass, Mg/MgO, Mg/SiO2, In/glass etc.) are reported. The interfaces were formed at plastic deformation of metal on the oxide surface at room temperature. Their structure, chemical composition, and micromechanical properties were studied by the AFM, XRD, SIMS, optical microscopy, and precision microindentation techniques. A noticeable adhesion was observed for metals with high affinity for oxygen and only in the regions of the maximum shear stress. Formation of an interfacial reaction zone with an oxygen concentration gradient is detected. In this zone metals are nanostructured and noticeably hardened. The effect…
On the Heuristic Procedure to Determine Processing Parameters in Additive Manufacturing Based on Materials Extrusion
2020
We present a heuristic procedure for determining key processing parameters (PPs) in materials-extrusion-based additive manufacturing processes. The concept relies on a design-of-experiment approach and consists of eleven &ldquo
Properties of ZnO coatings obtained by mechanoactivated oxidation
2009
In this work a new method based on the mechanoactivated oxidation has been applied for obtaining thin nanostructured transparent ZnO coatings on glass. Zn has been transferred onto a glass substrate at room temperature using a quickly rotating steel wire brush. Afterwards by subsequent annealing it is modified into a transparent ZnO coating. The temperature range in which formation of the needle-like (whiskers) structure and transition to the fine-grained structure occurs has been determined. The interrelation between physical properties and the change of microstructure of the ZnO coatings has been shown.
Low-K factor of SiO2 layer on Si irradiated by YAG:Nd laser
2007
Abstract The change of optical and electrical properties of SiO2 layer on Si single crystal exposed to YAG:Nd laser radiation has been found experimentally. The second harmonic of YAG:Nd laser was used as a source of light. Before irradiation the SiO2 layer with thickness 0.75 μm had red color in reflecting light due to the interference. After irradiation with the laser with intensity of more than 3.5 MW/cm2 red color changed to yellow. However, samples with thickness 0.21 μm did not change color after irradiation. We explain such peculiarities of optical properties by change of optical path. Capacity (C) measurements of SiO2 layer with thickness 0.21 μm by the method of capacity–voltage ch…
Evidence of nickel ions dimerization in NiWO$_4$ and NiWO$_4$-ZnWO$_4$ solid solutions probed by EXAFS spectroscopy and reverse Monte Carlo simulatio…
2021
G.B. acknowledges the financial support provided by the State Education Development Agency for project No.1.1.1.2/VIAA/3/19/444 (agreement No. 1.1.1.2/16/I/001) realized at the Institute of Solid State Physics, University of Latvia. A.K. and A.K. would like to thank the support of the Latvian Council of Science project No. lzp-2019/1-0071. Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART2.