Size-selective incorporation of DNA nanocages into nanoporous antimony-doped tin oxide materials.
A conductive nanoporous antimony-doped tin oxide (ATO) powder has been prepared using the sol-gel method that contains three-dimensionally interconnected pores within the metal oxide and highly tunable pore sizes on the nanoscale. It is demonstrated that these porous materials possess the capability of hosting a tetrahedral-shaped DNA nanostructure of defined dimensions with high affinity. The tunability of pore size enables the porous substrate to selectively absorb the DNA nanostructures into the metal oxide cavities or exclude them from entering the surface layer. Both confocal fluorescence microscopy and solution FRET experiments revealed that the DNA nanostructures maintained their int…
Preparation of Nanoporous MgAl2O4 by Combined Utilization of Sol-Gel Process and Combustion of Biorenewable Oil
ABSTRACTNanoporous MgAl2O4 particulates with high porosities were successfully prepared from sol-gel reactions, solvent exchange with castor oil and subsequent combustion and calcination at 700 °C. The products were crystalline and semitransparent. Changes in the metal precursor concentrations allowed control of pore volumes from 0.7 to 1.1 cm3/g and average pore sizes from 14 to 19 nm. The specific surface areas are about 200 m2/g regardless of the precursor concentrations. After heating at 1000 °C for 10 hours, the products kept about 70% of their original pore volume and about 60% of the original surface area. Heating at 1100 °C caused a drastic reduction of pore volume and surface area …