Synthesis of mesoporous silica nanoparticles (MSNs) and encapsulation of cisplatin for targeted cancer therapies
The aim of this PhD thesis is to elaborate mesoporous silica nanoparticles (MSNs) able to sustain the release of cisplatin into the intracellular compartments of solid tumors. The parametric study shows that morphological, structural and textural properties of MSNs-MCM-41, synthesized by sol-gel reaction by using TEOS as a silica source and CTAB as a structure-directing agent, depend on pH, stirring speed, temperature and extraction process of CTAB. The synthesis atmosphere has to be controlled in order to avoid the presence of ethanol and carbonate species which are responsible of necks between particles generating unstable suspensions of MSNs.MSNs were functionalized in order to control t…
Optimization of MCM-41 type silica nanoparticles for biological applications: Control of size and absence of aggregation and cell cytotoxicity
Abstract Mesoporous silica nanoparticles were synthesized at high pH using CTAB as a template and TEOS as a silica precursor. It was shown that varying the NaOH concentration between 5 and 27.5 mM allows the size, pore and silica structure of mesoporous nanoparticles to be precisely tuned. In particular, monodisperse nanoparticles with the MCM-41 structure with size ranging from 90 nm to 450 nm were obtained by increasing the NaOH concentration from 12.5 to 22.5 mM. It thus demonstrates that NaOH concentration must range between 12.5 and 15 mM in order to prepare MCM-41 silica nanoparticles with optimal size for nanovectorization. We also found that under usual conditions the aggregation of…