Electroplated Ni/Ni-Co multilayer coatings for higher corrosion-erosion resistance
Erosion-corrosion behaviour of hierarchical structured hydrophobic nickel-cobalt coating, obtained by electrodeposition, was assessed. In situ electrochemical measurements were carried out to study the corrosion resistance and stability during erosion tests. The electrochemical behaviour was related to surface hydrophobicity and its hierarchical structure nature as well as its modification. The pure Ni showed the lowest erosion-corrosion resistance. A smoothing of the hierarchical structure and thus a reduction the hydrophobicity was highlighted. On the other hand, Ni-Co coating even if associated to a lower electrochemical stability showed a more stable hierarchical structure also at high …
Assessment of performance degradation of hybrid flax-glass fiber reinforced epoxy composites during a salt spray fog/dry aging cycle
The main goal of this paper is the evaluation of the performances reversibility of hybrid composites when they are dried after being aged in salt-fog environment. To this aim, epoxy composites reinforced with flax and glass fabrics respectively in the internal and external laminae were at first exposed to salt-fog (i.e., identified as wet phase) and then stored in controlled conditions (i.e., identified as dry phase). The flexural properties evolution of these composites as well as their water uptake and contact angle were monitored at varying time of both phases. The flexural strength and modulus of hybrid composites is 23.4% (17.9%) and 15.5% (12.9%) lower than unaged ones after 30 (15) d…
An experimental investigation on performances recovery of glass fiber reinforced composites exposed to a salt-fog/dry cycle
The main goal of this paper is the evaluation of the properties reversibility of glass fiber reinforced polymers (GFRPs) under discontinuous exposure to aggressive environmental conditions, typical of marine applications. To this aim, the GFRP manufactured through vacuum infusion process has been initially aged in humid conditions (i.e., exposure to salt-fog at 35 ◦C) for 15 and 30 days and then stored under controlled dry conditions (i.e., 50% R.H. and 23 ◦C) for times varying between 0 and 21 days. In order to evaluate the recover capability of this material, its water uptake has been monitored along the quasi-static flexural properties during the entire humid/dry cycle. Moreover, both 3D…
Wettability of flax/basalt reinforced composites during aging in salt spray conditions
Aim of this work was to investigate the wettability of natural fibres reinforced epoxy composites, subjected to aging tests performed on two different laminates. The first laminate was constituted by stacking ten layers of bidirectional flax fabrics. The second one was produced by replacing two external flax layers with two layers of basalt mat, for each side of the laminate. Both laminates were exposed to salt-fog environmental conditions, according to ASTM B 117 standard, for 60 days. The results of wettability were compared with those of the water uptake test. Moreover, an analysis of variance was performed in order to evaluate the significance of the parameters that influence the wettab…