Optical properties of the low-molecular amorphous azochromophores and their application in holography
The films based on the low-molecular amorphous azochromophore 2-(3-(4-((4- (Ethyl(2-(trityloxy)ethyl)amino)phenyl)diazenyl)styryl)-5,5-dimethylcyclohex-2-enylidene) malononitrile (IWK-2M) were prepared. The optical properties of the material, such as transmittance and reflection spectra of the film, sensitivity to polarization holographic recording by two wavelengths (405 and 532 nm) were studied. The direct relief formation during the polarization holographic recording was explored, relief depth dependence on exposure and record beam intensity was investigated. The holographic matrix on this material base was produced without chemical etching process; the replication of holographic image w…
Investigations of As-S-Se thin films for use as inorganic photoresist for digital image-matrix holography
AbstractAs-S-Se chalcogenide thin films are successfully employed in classical and dot-matrix holography as inorganic photoresists for obtaining a relief-phase hologram. However using these films for image-matrix hologram recording has not been studied due to some features of image-matrix technology. For the applied research of the optical properties of As-S-Se films an experimental device of digital image-matrix holographic recording based on 100 mW 405 nm semi-conductor laser and Spatial Light Modulator (SLM) has been created. The device has the following main parameters: 140 × 105 µm frame size; laser intensity during exposure 10 W/cm2. With the help of this device diffraction grating an…
Photosensitive properties of composite films based on copper chloride in polymer matrix
The composite films based on PMMA and CuCl2 were prepared. Transmission spectra of the films before and after illumination by different laser lines (405, 448, 456 nm) were measured. The reversible character of the composite photosensitivity was fixed. The phenomenon of direct surface relief formation after laser beam illumination of composite films was described. The holographic gratings were recorded by different exposure (200 – 500 J/cm2) in the films with different concentration (8 and 20 wt. %) of copper salt. The film sensitivity dependence on polymer molecular weight was studied. Surface relief of the gratings was measured by AFM.
<title>Dot-matrix holographic recording in amorphous chalcogenide films</title>
We have developed PC controlled dot-matrix holographic recording system based on the CW diode pumped YAG:Nd SHG laser (wavelength 532 nm, power 30mW,) modulated electronically with TTL signals. Two-beam technique has been used with convergence angle 30o and PC controlled incident beam plane rotation 0-360o. Optical system consists of beam splitter, 40mm focus length forming cylindrical lens and 40mm focusing lens. Characteristic parameters of experimental equipment are following: spot size - 50-200 micrometers, direct laser writing area, limited by x-y positioning system, was 70mm x 70mm, number of writing head rotation positions up to 256 (8 bit), time of each exposure - 1-1000 msec. As th…
A non-enzymatic electrochemical hydrogen peroxide sensor based on copper oxide nanostructures
This work was supported by ERDF project No. 1.1.1.2/16/I/ 001, research application number 1.1.1.2/VIAA/4/20/743 "Development of nanomaterial-based electrochemical sensor for detection of hydrogen peroxide". Institute of Solid State Physics, University of Latvia as the Center of Excellence has received fund ing from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017 TeamingPhase2 under grant agree ment No. 739508, project CAMART2.
<title>Investigation of As<formula><inf><roman>2</roman></inf></formula>S<formula><inf><roman>3</roman></inf></formula>-Al films for dot-matrix holographic recording</title>
We have performed the investigation of dot matrix holographic recording in amorphous As2S3 chalcogenide films with different thickness on Al coated glass substrates. The control over the interference minimum of reflection during the evaporation process allowed obtaining As2S3-Al system with a minimum value of initial reflection in defined spectral region. The investigation of dependence of diffraction efficiency of holographic recording on both film thickness and initial conditions of reflectivity in the system was performed. The main advantage of this type of system is the possibility to increase optical sensitivity of material in predefined spectrum region for phase hologram recording.© (…