Ultrasonic phased array inspection of wire plus arc additive manufacture samples using conventional and total focusing method imaging approaches
In this study, three aluminium samples produced by wire + arc additive manufacture (WAAM) are inspected using ultrasonic phased array technology. Artificial defects are machined using a centre drill, ø 3 mm, and electrical discharge machining (EDM), ø 0.5-1 mm, in a cylindrical through-hole topology. The samples are first inspected using a single-element wheel probe mounted on a KUKA robot in order to investigate the feasibility of using a conventional ultrasonic transducer approach. Unfortunately, the wheel probe is found to be unsuitable for scanning the WAAM specimens and ultrasonic phased arrays are employed next. The set-up includes 5 MHz and 10 MHz arrays (128 elements) in direct cont…
Ultrasonic phased array inspection of a Wire + Arc Additive Manufactured (WAAM) sample with intentionally embedded defects
In this study, Wire + Arc Additive Manufacture (WAAM) was employed to manufacture a steel specimen with intentionally embedded defects which were subsequently used for calibration of an ultrasonic phased array system and defect sizing. An ABB robot was combined with the Cold Metal Transfer (CMT) Gas Metal Arc (GMA) process to deposit 20 layers of mild steel. Tungsten-carbide balls (ø1-3 mm) were intentionally embedded inside the additive structure after the 4th, 8th, 12th and 18th layers to serve as ultrasonic reflectors, simulating defects within the WAAM sample. An ultrasonic phased array system, consisting of a 5 MHz 64 Element phased array transducer, was used to inspect the WAAM sample…
Ultrasonic phased array inspection of wire plus arc additive manufacture (WAAM) samples using conventional and total focusing method (TFM) imaging approaches
In this study, three aluminium samples produced by wire + arc additive manufacture (WAAM) are inspected using ultrasonic phased array technology. Artificial defects are machined using a centre drill, ø3 mm, and electro-discharge machining (EDM), ø0.5-1 mm, in a cylindrical through hole topology. The sample was first inspected by a single element wheel probe mounted on a KUKA robot in order to investigate the feasibility of using a conventional ultrasonic transducer approach. Unfortunately, the wheel probe was found to be unsuitable for scanning of the WAAM specimens and ultrasonic phased arrays were employed next. The setup included 5 MHz and 10 MHz arrays (128 elements) in direct contact w…