Ultrasonic phased array inspection of wire plus arc additive manufacture samples using conventional and total focusing method imaging approaches
In this study, three aluminium samples produced by wire + arc additive manufacture (WAAM) are inspected using ultrasonic phased array technology. Artificial defects are machined using a centre drill, ø 3 mm, and electrical discharge machining (EDM), ø 0.5-1 mm, in a cylindrical through-hole topology. The samples are first inspected using a single-element wheel probe mounted on a KUKA robot in order to investigate the feasibility of using a conventional ultrasonic transducer approach. Unfortunately, the wheel probe is found to be unsuitable for scanning the WAAM specimens and ultrasonic phased arrays are employed next. The set-up includes 5 MHz and 10 MHz arrays (128 elements) in direct cont…
Multi-aperture beamforming for automated large structure inspection using ultrasonic phased arrays
Increasing the inspection quality and speed is essential in manufacturing applications, especially for large structures (e.g. modern aircrafts). Traditional ultrasonic manual scanning can be comprehensive, but lacks repeatability and is time-consuming. Several robotic non-destructive testing systems have been developed in recent years. Although high inspection rates have been achieved by the use of robotic arms, there is the need to furtherly increase the inspection speeds, to cope with the current industrial demands. For systems delivering robotic ultrasonic inspection through phased array probes, the current bottleneck is given by the time required to electrically fire all elements of the…
Robotic geometric and volumetric inspection of high value and large scale aircraft wings
Increased demands in performance and production rates require a radical new approach to the design and manufacturing of aircraft wings. Performance of modern robotic manipulators has enabled research and development of fast automated non-destructive testing (NDT) systems for complex geometries. This paper presents recent outcomes of work aimed at removing the bottleneck due to data acquisition rates, to fully exploit the scanning speed of modern 6-DoF manipulators. The geometric assessment of the parts is carried out with a robotised dynamic laser scanner encoded through an absolute laser tracker. This method allows scanning speeds up to 330mm/s at 1mm pitch. State of the art ultrasonic ins…
Intentional weld defect process: From manufacturing by robotic welding machine to inspection using TFM phased array
Specimens with intentionally embedded weld defects or flaws can be employed for training, development and research into procedures for mechanical property evaluation and structural integrity assessment. It is critical that the artificial defects are a realistic representation of the flaws produced by welding. Cylindrical holes, which are usually machined after welding, are not realistic enough for our purposes as it is known that they are easier to detect than the naturally occurring imperfections and cracks. Furthermore, it is usually impractical to machine a defect in a location similar to where the real weld defects are found. For example, electro-discharge machining can prod…
Ultrasonic phased array inspection of a Wire + Arc Additive Manufactured (WAAM) sample with intentionally embedded defects
In this study, Wire + Arc Additive Manufacture (WAAM) was employed to manufacture a steel specimen with intentionally embedded defects which were subsequently used for calibration of an ultrasonic phased array system and defect sizing. An ABB robot was combined with the Cold Metal Transfer (CMT) Gas Metal Arc (GMA) process to deposit 20 layers of mild steel. Tungsten-carbide balls (ø1-3 mm) were intentionally embedded inside the additive structure after the 4th, 8th, 12th and 18th layers to serve as ultrasonic reflectors, simulating defects within the WAAM sample. An ultrasonic phased array system, consisting of a 5 MHz 64 Element phased array transducer, was used to inspect the WAAM sample…
Ultrasonic phased array inspection of wire plus arc additive manufacture (WAAM) samples using conventional and total focusing method (TFM) imaging approaches
In this study, three aluminium samples produced by wire + arc additive manufacture (WAAM) are inspected using ultrasonic phased array technology. Artificial defects are machined using a centre drill, ø3 mm, and electro-discharge machining (EDM), ø0.5-1 mm, in a cylindrical through hole topology. The sample was first inspected by a single element wheel probe mounted on a KUKA robot in order to investigate the feasibility of using a conventional ultrasonic transducer approach. Unfortunately, the wheel probe was found to be unsuitable for scanning of the WAAM specimens and ultrasonic phased arrays were employed next. The setup included 5 MHz and 10 MHz arrays (128 elements) in direct contact w…