Effect of latex on surface structure and wetting of pigment coatings
Abstract The amount and type of latex binder has a significant effect on both the structure and chemical properties of pigment coatings, which affects critical surface properties, e.g., gloss, ink setting rate via liquid absorption, and spreading properties. Increased knowledge is required for improved optimization in practical applications of pigment coating layers. To this end, the effect of binder amount for two different styrene–butadiene latices in kaolin pigment coatings on a base paper was studied, by measuring the surface topography, surface chemistry, and liquid absorption of these coatings. The topography was thoroughly analyzed from nanometer to millimeter length scales by atomic…
Wettability and compositional analysis of hydroxyapatite films modified by low and high energy ion irradiation
Abstract Hydroxyapatite-like thin films on silicon substrate were deposited using atomic layer deposition and were subjected to irradiation with Ar ions accelerated through 0.6–1.2 kV as well as 2 MeV 16 O + ions. After low energy Ar irradiation a significant reduction in contact angle was observed. However, the Ca/P atomic ratio remained unchanged. No reduction in contact angle was seen for high energy 16 O + irradiation. Atomic force microscopy showed the enhancement of floral-like pattern after low energy Ar bombardment while high energy oxygen irradiation lead to raised islands on as-deposited films.