MECHANICAL, RHEOLOGICAL AND THERMAL EVALUATION OF POLY(LACTIC ACID) (PLA)/MICRO FIBRILLATED CELLULOSE (MFC) PLASTICIZED BIOCOMPOSITES PRODUCED WITH FLAT DIE EXTRUSION AND CALENDERING
The use of Micro Fibrillated Cellulose (MFC) as filler for polymeric matrices attempts an increasing interest both in academia and industry. In this framework, encouraging results have been obtained using plasticizers, as dispersing aids, during twin-screw extrusion that optimizes the process parameters and avoid MFC agglomeration. In this work, two commercial typologies of waterborne solution of MFC (Exilva and Celish) were melt-compounded in a PLA matrix through semi-industrial twin-screw extruder and calendered, producing films of 150 μm thickness. These films were mechanically and thermally characterized, moreover the migration of the plasticizer along the time was evaluated through ana…
Effect of the UV exposure on the creep behaviour of PLA based green composites
Green composites made of biodegradable matrices and lignocellulosic fibers are receiving growing attention from both academia and industries. Despite a wide literature can be found about mechanical behavior of such kind of composites, at the best of our knowledge, only limited information is available about their creep behavior [1] and no papers have been yet done on the effect of ultraviolet exposition. The tensile creep behavior at 40 °C of PLA based composites, containing flax and jute twill weave woven fabrics, produced through compression molding, was investigated. As preliminary characterization, quasi-static tensile tests were carried out on virgin and UV aged composites