Large scale synthesis of nanostructured zirconia-based compounds from freeze-dried precursors
Nanocrystalline zirconia powders have been obtained at the multigram scale by thermal decomposition of precursors resulting from the freeze-drying of aqueous acetic solutions. This technique has equally made possible to synthesize a variety of nanostructured yttria or scandia doped zirconia compositions. SEM images, as well as the analysis of the XRD patterns, show the nanoparticulated character of those solids obtained at low temperature, with typical particle size in the 10–15 nm range when prepared at 673 K. The presence of the monoclinic, the tetragonal or both phases depends on the temperature of the thermal treatment, the doping concentration and the nature of the dopant. In addition,…
Nanostructured Alumina from Freeze-Dried Precursors
Nanocrystalline alumina has been obtained on the 100 g scale by thermal decomposition of precursors resulting from the freeze-drying of aqueous solutions of different aluminum-containing products, namely aluminum acetate and aluminum L-lactate. Samples prepared at different temperatures (from 873 to 1573 K in steps of 100 K) were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and surface area measurements. In the acetate case, the transformation sequence involves the formation of θ-Al 2 O 3 as an intermediate phase between γ-Al 2 O 3 and α-Al 2 O 3 , whereas this θ phase is not observed in the lactate case. TEM…