Correlation between processability and properties of a high density polyethylene by a rheological approach
The thermal-oxidative and thermal-mechanical stability of high density polyethylene (chromium based catalyst technology) was examined at many different temperatures using a rheological approach. The changes in molecular structure, which take place during processing, have been studied using a Clextral co-rotating twin-screw extruder in comparison with dynamic measurements performed with a rotational rheometer under definite conditions of temperature, strain and frequency and in presence of air. In order to evaluate the degradation response, an investigation of elastic modulus G' as a function of frequency ω on the residual sample after ageing has been carried out. The molecular weight increa…
On the modification of the nitrile groups of acrylonitrile/butadiene/styrene into oxazoline in the melt
Oxazoline functionality is well known to be highly reactive toward a lot of other functional groups like carboxyls, hydroxyls, mercaptans, and amines. In this work we report the possibility to modify the nitrile groups of an acrylonitrile/butadiene/styrene (ABS) copolymer into oxazoline in the molten state in the presence of aminoethanol as modifier agent and zinc acetate as a catalyst. The reaction has been carried out in a batch mixer and in a corotating twin screw extruder. The conversion of the nitrile groups into oxazoline has been verified by infrared spectroscopy, NMR analysis microanalysis and confirmed by thermomechanical characterization. The results indicate that the kinetic of g…
Melt stabilisation of high-density film-grade polyethylene
The thermoxidative degradation of a high-density polyethylene stabilised either with standard and novel kinds of antioxidants was examined at many different temperatures. The aim of this work was to investigate the degradation response (crosslinking or chain-breakage) on the polyolefin molecular structure in terms of low shear rate melt viscosity increment and oxidation induction time both studied through steady and dynamic shear flow tests performed in a rotational rheometer. Lactone type antioxidants, especially the one containing P-EPQ phosphite component, exhibit the lowest thermoxidative degradation at high temperatures. Vitamine E, used in blend with a phosphite, appears to be a good …
The antioxidant effect in controlling thermal degradation of a low density polyethylene blown film
Abstract It is well known that antioxidants are widely used to prevent thermal degradation of high density and linear low density polyethylene. Antioxidants are not always present in low density polyethylene and only small amounts are usually added to these resins. In this work the effect of an antioxidant system on a low density resin having MFI (190 °C/2.16 kg)=2 g/10′ and density 0.9230 g/cm3 has been studied. Its effect on melt viscosity has been studied by means of a batch mixer and the torque vs time behaviour has been analysed. The results show that a maximum in the torque vs time curve can be seen for the material containing antioxidant. In contrast, the material without antioxidant…
Radiation grafting functionalization of poly (vinylidene fluoride) to compatibilize its blends with polyolefin ionomers
Blends of a crystalline vinylidene fluoride copolymer (PVDF) and a polyolefin ionomer were produced by melt mixing and characterized by a variety of techniques to examine the effect of increasing the level of salt formation on morphology. The PVDF component was also grafted with methacrylic acid by irradiating the polymer powder and subsequently treating it with an aqueous monomer solution. The effect of neutralizing the acid in both polymer components to produce the corresponding zinc salt was also investigated. Compatibilization was accomplished by the addition of zinc acetyl acetonate (ZnAcAc) to the mixture. This increased the viscosity of the polyolefin ionomer phase, comparable to tha…
Rheological Properties of Different Film Blowing Polyethylene Samples Under Shear and Elongational Flow
Summary: The rheological behavior of polyethylenes ismainly dominated by the molecular weight, the molecularweight distribution and by the type, the amount and thedistribution of the chain branches. In this work a linearmetallocenecatalyzedpolyethylene(m-PE),abranchedme-tallocene catalyzed polyethylene (m-bPE), a conventionallinear low density polyethylene (LLDPE) and a low densitypolyethylene (LDPE) have been investigated in order tocompare their rheological behavior in shear and in elonga-tional flow. The four samples have similar melt flow indexand in particular a value typical of film blowing grade.The melt viscosity has been studied both in shear and inisothermal and non-isothermal elonga…