Strontium and iron-doped barium cobaltite prepared by solution combustion synthesis: exploring a mixed-fuel approach for tailored intermediate temperature solid oxide fuel cell cathode materials
Ba0.5Sr0.5Co0.8Fe0.2O3-? (BSCF) powders were prepared by solution combustion synthesis using single and double fuels. The effect of the fuel mixture on the main properties of this well-known solid oxide fuel cell cathode material with high oxygen ion and electronic conduction was investigated in detail. Results showed that the fuel mixture significantly affected the area-specific resistance of the BSCF cathode materials, by controlling the oxygen deficiency and stabilizing the Co2+ oxidation state. It was demonstrated that high fuel-to-metal cations molar ratios and high reducing power of the combustion fuel mixture are mainly responsible for the decreasing of the area-specific resistance o…
Cutting performance and indentation behaviour of diamond films on Co-cemented tungsten carbide
Abstract Diamond films were grown by Hot Filament Chemical Vapour Deposition (HFCVD) on differently pretreated ISO-grade K10 cemented carbide (WC-5.8 wt.%Co) cutting inserts. Etching with diluted HNO3 and surface roughening by Murakami's reagent were used as substrate pretreatments. The adhesion of the films was evaluated by indentation tests. In order to obtain a reliable estimation of the adhesion by the slope of the crack radius–indentation load curves, a careful SEM measurement of the crack lengths was performed. Bare and diamond-coated cutting inserts were used for turning tests of Al2O3-reinforced aluminum alloy. The adhesion levels obtained from the indentation curves correlated well…