Uso di idrotalciti in compositi a matrice PLA preparati nel fuso

Comparison of Different Processing Methods to Prepare Poly(lactid acid)–Hydrotalcite Composites

The effect of the compounding method on the morphology and on the properties of poly(lactic acid) (PLA)-hydrotalcite (HT) composites was studied. Moreover, the influence of two different kinds of HT - organically modified (OM-HT) and unmodified (U-HT) - and their concentration was evaluated. The composites were prepared using either a single screw extruder (SSE), a counter rotating twin-screw compounder (TSC) or a corotating twin-screw extruder (TSE). The prepared materials were characterized by scanning electron microscopy, gel permeation chromatography (GPC) analysis, mechanical and rheological measurements. The results indicated that the best morphology, i.e., particles dimension and dis…

Effects of phenolic-like intercalated layered double hydroxides on poly(lactic acid) based nanocomposites

Two phenolic-like antioxidants (AOs), 3-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate and 6-hydroxy-2,5,7,8-tetrametilcromano-2-carboxylate anions, were intercalated by anion exchange in layered double hydroxides (LDHs). The two AO-LDHs were dispersed by ultrasound-assisted solution mixing in poly(lactic acid) (PLA) and the thermal oxidation stability of the composites was evaluated following the variation of the molecular weight by SEC, after a controlled aging process, and determining the oxidation induction time (OIT) by DSC. The results evidenced that the intercalation of both the AO molecules within the LDH galleries prevent their own thermal and thermo-oxidative degradation as well a…