Different kinds of solid solutions in the V2O5-ZrSiO4-NaF system by sol-gel processes and their characterization
Abstract In the V2O5-ZrSiO4-NaF system, three kinds of substances have been identified by sol-gel methods depending on the V2O5 amounts in the composition. Their characterization by X-ray diffraction, measurements of unit cell parameters, UV-visible (UV-V) spectroscopy, differential thermal analysis and lab colour parameter determination allow the consideration of three kinds of solid solution in the zircon lattice: (a) V+5,V+4-ZrSiO4, thermally stable and with a deep green colour; (b) V+4-ZrSiO4, thermally stable and blue coloured, made by the sol-gel method and with V2O5 amounts lower than 0·03 mol per formula weight; and (c) Na+,F−,V+4-ZrSiO4, a solid solution with a deep blue-turquoise …
Cobalt aluminate spinel-mullite composites synthesized by sol-gel method
Abstract CoAl 2 O 4 spinel-mullite composites were prepared by double substitution of Al by Ti and Ni in stoichiometric 3:2 mullite. Gels with compositions 3(Al 2 − 2 x Co x Ti x O 3 )·2SiO 2 (x = 0.025, 0.05 and 0.2) and 3(Al 2 − 2 x M x O 3 )·2SiO 2 (x = 0.05; M = Co 2+ or Ti 4+ ) were synthesized by sol-gel techniques. The structure of the gels was investigated by infra-red spectroscopy. Heating gels at 750 °C produced an amorphous silicoaluminate network. The reaction sequence was investigated by differential thermal analysis, X-ray diffraction and ultraviolet-visible spectroscopy. All samples crystallized at temperatures lower than 1000 °C from the amorphous state. Al-Si spinel and/or …
Synthesis and characterization of V2O5SiO2ZrO2 pigments by sol-gel method
Abstract Polymeric gels in the V2O5 SiO2 ZrO2 system were prepared from tetraethylorthosilicate (TEOS), zirconium(IV)-n-propoxide and vanadium(IV) oxyacetylacetonate, precursors. The effects of prehydrolysis time of TEOS and drying gel method on the stabilization of tetragonal zirconia in the silica amorphous matrix, nucleation and growth of the zircon (ZrSiO4) phase, and stabilization of the blue and green stains of vanadium zircon were studied. Results provide evidence that long time of prehydrolysis and fast drying do not favour zircon crystallization but stabilize the tetragonal zirconia in the amorphous matrix.
Spinel-mullite composites with optical properties
The aim of this paper was to study the synthesis and characterization of spinel-containing mullite based materials, using sol-gel techniques. Several gels were prepared, with nominal compositions 3(Al2−2xMx TixO3)·2SiO2 and 3(Al2−xMxO3)·2SiO2, with M=Ni+2 or Co+2 and 0.0≤x≤0.2, by hydrolysis and condensation of mixtures of aluminum, silicon and titanium alkoxides and nickel chloride. Dried gels were homogeneous and displayed a glass transition at around 750°C, which indicated that the system could be described as an amorphous silicoaluminate network.
Reaction Sequence in the Preparation of NiAl2O4 Spinel-Mullite Composites by Sol-Gel
NiAl 2 O 4 spinel-mullite composites were prepared by simultaneous replacement of Al by Ti and/or Ni in 3:2 stoichiometric mullite. Specimens having nominal compositions 3(Al 2-2x Ni x Ti x O 3 ).2SiO 2 (x = 0, 0.025, 0.05, 0.2) and 3(Al 2-x M x O 3) .2SiO 2 (M = Ni 2+ or Ti 4+ and x = 0.05) were synthesized by sol-gel techniques, which provide homogeneous gels in the SiO 2 -Al 2 O 3 system. Gel structures investigated by infrared (IR) spectroscopy revealed the formation of Al-O-Si bonds in dried gels. The reaction sequence of gel-derived glasses, previously obtained by preheating gels at 750°C for 3 h, was evaluated by X-ray powder diffraction (XRD) and ultraviolet-visible (UV-vis) spectro…
Effect of NiO and/or TiO2 mullite formation and microstructure from gels
Polymeric and colloidal gels with a constant molar ratio of (Al+Ni and/or Ti)/Si=3/1 and various (Al/Ni and/or Ti) ratios (up to 21.42 mol% NiO+TiO2) were prepared and used to study the effect of the precursor chemical homogeneity on mullite formation processes and the resulting microstructure. Both kinds of gel precursors were preheated at 750°C for 3 h in order to obtain appropriate gel-derived glasses for further thermal processing. After annealing for several time periods at temperatures between 750 and 1500°C, differences in crystallization pathways were observed. Polymeric gels crystallized Al–Si and NiAl2O4 spinels from the amorphous form at temperatures in the range between 900 and …