0000000000225778
AUTHOR
Mauro Ricotta
Investigation of the crack tip stress field in a stainless steel SENT specimen by means of Thermoelastic Stress Analysis
Abstract In this work a Thermoelastic Stress Analysis (TSA) setup is implemented to investigates the Thermoelastic and Second Harmonic signals on a fatigue loaded Single Edge Notched Tension (SENT) specimen made of stainless steel AISI 304L. Three load ratios are in particular applied, R=-1, 0, 0.1. The thermoelastic signal is used to evaluate the Stress Intensity Factor via two approaches, the Stanley-Chan linear interpolation method and the over-deterministic least-square fitting (LSF) method using the Williams’ series expansion. Regarding least-square fitting, an iterative procedure is proposed to identify the optimal crack tip position in the thermoelastic maps. The SIF and T-Stress are…
On the correlation of temperature harmonic content with energy dissipation in C45 steel samples under fatigue loading
Fatigue damage onset involves a transformation of mechanical energy. This is in part spent into work of plastic deformation and fracture and in part transformed into heat. Therefore, different thermomechanical heat sources are activated during a fatigue loading cycle, resulting in a temperature modulation that can be characterized by its frequency content. Several studies have monitored the temperature on samples undergoing high-cycle fatigue, measuring specific thermomechanical metrics which could serve as indicators of damage evolution. The present work evaluates the harmonic content of temperature, to investigate its correlation with the material dissipation. The harmonic terms investiga…
On relation between J-integral and heat energy dissipation at the crack tip in stainless steel specimens
In this paper, an experimental procedure to evaluate the elastic-plastic J-integral at the tip of a fatigue crack is presented. According to this new approach, the elastic component of the J-integral is derived from Thermoelastic Stress Analysis, while the plastic component of the J-integral is derived from the heat energy loss. An analytical link is proposed to apply this new experimental technique. Therefore, the elastic-plastic J-integral range was evaluated starting from infrared temperature maps measured in situ during crack propagation tests of AISI 304L stainless steel specimens. It was found that the range of the infrared thermography-based J-integral correlated well the crack growt…
Infrared thermography-based evaluation of the elastic-plastic J-integral to correlate fatigue crack growth data of a stainless steel
Abstract The elastic-plastic J-integral is adopted to correlate fatigue crack growth data of ductile metals. An analytical link is known to exist between the J-integral and the strain energy density averaged in a control volume embracing the crack tip. On the other hand, the strain energy fluctuation is the source of temperature variations close to a fatigue crack tip of a metal material; hence the possibility to measure the J-integral from infrared thermographic scanning at the crack tip is envisaged and it is the focus of this paper. It is proposed that the elastic component of the J-integral is derived from a thermoelastic stress analysis, while the plastic component of the J-integral is…