Time-resolving Analysis of Cryotropic Gelation of Water/Poly(Vinyl Alcohol) Solutions via Small Angle Neutron Scattering
2007
The structural transformations occurring in initially homogeneous aqueous solutions of poly(vinyl alcohol) (PVA) through application of freezing (-13 degrees C) and thawing (20 degrees C) cycles is investigated by time resolving small-angle neutron scattering (SANS). These measurements indicate that formation of gels of complex hierarchical structure arises from occurrence of different elementary processes, involving different length and time scales. The fastest process that could be detected by our measurements during the first cryotropic treatment consists of the crystallization of the solvent. However, solvent crystallization is incomplete, and an unfrozen liquid microphase more concentr…
Slow Crystallization Kinetics of Poly(vinyl alcohol) in Confined Environment during Cryotropic Gelation of Aqueous Solutions
2006
The gelation kinetics of aqueous solutions of poly(vinyl alcohol) (PVA) during freezing at −13 °C has been investigated with time-resolved small angle neutron scattering. Crystallization of PVA takes place inside an unfrozen liquid microphase that forms in the matrix of ice crystals and follows a first-order kinetics during the early stages and becomes very slow in the later stages with an apparent Avrami exponent lower than 1. Crystallization of PVA at low temperatures is responsible of formation of strong physical gels upon defrosting, provided that the concentration of PVA is higher than a critical value.
Mesoscopic and Microscopic Investigation on Poly(vinyl alcohol) Hydrogels in the Presence of Sodium Decylsulfate
2007
The structure of poly(vinyl alcohol) (PVA) hydrogels formed as a result of freeze/thaw treatments of aqueous solutions of the polymer (11 wt % PVA) in the freshly prepared state is analyzed through the combined use of small (SANS) and ultrasmall (USANS) angle neutron scattering techniques. The structure of these hydrogels may be described in terms of polymer rich regions, with dimensions of the order of 1-2 microm, dispersed in a water rich phase, forming two bicontinuous phases. The PVA chains in the polymer rich phase form a network where the cross-linking points are mainly crystalline aggregates of PVA having average dimensions of approximately 45 A. The structural organization of freeze…