Shape-Dependence of Pd Nanocrystal Carburization during Acetylene Hydrogenation
This interdisciplinary work combines the use of shape- and size-defined Pd nanocrystals (cubes of 10 and 18 nm, and octahedra of 37 nm) with in situ techniques and DFT calculations to unravel the dynamic phenomena with respect to Pd reconstruction taking place during acetylene hydrogenation. Notably, it was found that the reacting Pd surface evolved at a different pace depending on the shape of the Pd nanocrystals, due to their specific propensity to form carbides under reaction conditions. Indeed, Pd cubes (Pd(100)) reacted with acetylene to form a PdC0.13 phase at a rate roughly 6-fold higher than that of octahedra (Pd(111)), resulting in nanocrystals with different degrees of carburizati…
Structure Sensitivity of 2-Methyl-3-butyn-2-ol Hydrogenation on Pd: Computational and Experimental Modeling
In the frame of DFT paradigms, the adsorption of 2-methyl-3-butyn-2-ol (MBY) and 2-methyl-3-buten-2-ol (MBE) on a Pd-30 cluster, including both {100} and {111} faces, was studied along with the pathways involved in the hydrogenation, taking place on plane and low coordination (corner/edge) sites of given MBY/Pd-30 and MBE/Pd-30 surface configurations. The calculated energetics, further validated by gas-phase and water-assisted gas-phase MBY and MBE hydrogenation, performed on well-defined size and shape-controlled Pd nanoparticles supported on SiO2, were able to explain the origin of the structure sensitivity and the high selectivity characterizing the title reaction when occurring in aqueo…