Co-precipitation of Mg-doped Ni0.8Co0.1Mn0.1(OH)₂:effect of magnesium doping and washing on the battery cell performance
Co-precipitation of Ni0.8Co0.1Mn0.1(OH)2 (NCM811) and Mg-doped (0.25 wt% and 0.5 wt%) NCM811 precursors is carried out from concentrated metal sulphate solutions. In this paper, the aim is to study the role of magnesium dopant in the co-precipitation step of NCM811, the cathode active material and further the Li-ion battery cell performance. Based on the results, magnesium was fully co-precipitated in the NCM811 precursors, as expected from thermodynamic calculations. The presence of magnesium in these precursors was also confirmed by several characterization methods and magnesium was evenly distributed in the sample. It was observed that tapped density decreased and surface area increased …
Correlation of aluminum doping and lithiation temperature with electrochemical performance of LiNi1-xAlxO2 cathode material
Abstract This article presents a process for producing LiNi1-xAlxO2 (0 < × < 0.05) cathode material with high capacity and enhanced cycle properties of 145 mAh/g after 600 cycles. The LiNi1-xAlxO2 (0 < × < 0.05) cathode material is prepared by mixing coprecipitated Ni(OH)2 with LiOH and Al(OH)3, followed by lithiation at temperature range of 650–710 °C, after which any residual lithium from lithiation is washed from the particle surfaces. Electrochemical performance was studied within full-cell and half-cell application; in addition, different material characterization methods were carried out to explain structure changes when certain amount of aluminum is introduced in the …
Effects of Lithium Source and Content on the Properties of Li-Rich Layered Oxide Cathode Materials
Lithium-rich layered oxide (LLO) are considered high-capacity cathode materials for next-generation lithium-ion batteries. In this study, LLO cathode materials were synthesized via the hydroxide coprecipitation method followed by a two-step lithiation process using different lithium contents and lithium sources. The effects of lithium content and lithium source on structure and electrochemical performance were investigated. This study demonstrated the clear impact of Li/TM ratio on electrochemical performance. Lower Li/TM ratio reduced the irreversible capacity loss in the first cycle and provided better cycling stability among all samples. The best results exhibited an initial discharge ca…
Precipitation and Calcination of High-Capacity LiNiO2 Cathode Material for Lithium-Ion Batteries
This article presents the electrochemical results that can be achieved for pure LiNiO2 cathode material prepared with a simple, low-cost, and efficient process. The results clarify the roles of the process parameters, precipitation temperature, and lithiation temperature in the performance of high-quality LiNiO2 cathode material. Ni(OH)2 with a spherical morphology was precipitated at different temperatures and mixed with LiOH to synthesize the LiNiO2 cathode material. The LiNiO2 calcination temperature was optimized to achieve a high initial discharge capacity of 231.7 mAh/g (0.1 C/2.6 V) with a first cycle efficiency of 91.3% and retaining a capacity of 135 mAh/g after 400 cycles. These a…