Formation of calcium containing minerals in the low temperature dolomite ceramics

In order to elaborate low temperature dolomite ceramics, potentially suitable for the production of building materials, local low carbonate clay and dolomite siftings were used as a raw materials. Relationship between mechanical properties, mineral composition and firing temperature kept in the range of 600-800° C were established. According to the obtained data it was detected that the optimal burning temperature, giving the highest crushing strength (40 MPa) was around 700-750° C, optimal proportion of dolomite and clay expressed as ratio between CaO and Al2O3 - 2.5 wt%. Gradual formation of C3A occurs during firing, yielding C4AHX, i.e. mainly C4AH13 after hydratation of obtained composi…