Nitrogen plasma pressure influence on the composition of TiNxOy sputtered films

Thin films of TiNxOy were deposited by d.c. magnetron sputtering on glass substrates using an (Ar+,N2) plasma and Ti target. The N2 partial pressure was changed from 2.3 × 10−4 mbar to 4.6 × 10−3 mbar in order to obtain films with increasing nitrogen contents. X-ray photoelectron spectroscopy was used to determine the as-deposited composition. The presence of oxygen, which is probably due to contamination from the residual atmosphere in the vacuum chamber, is always detected, both in the surface layers and in the bulk of the films, confirming the formation of TiNxOy. When the nitrogen partial pressure was increased, a maximum for the nitrogen content in the films was reached, corresponding …