Time-resolved pulsed OSL of ceramic YAP:Mn phosphors
2019
The paper deals with the results of comparative study on time-resolved pulsed optically stimulated luminescence (TR-OSL) response of ceramic YAP:Mn materials prepared by different methods. In parti...
Stable and transient color centers in Gd3Ga5O12 crystals
2004
The work is devoted to investigation of stable color centers (CC) that are created in Gd3Ga5O12 (GGG) crystals under irradiation with γ-quanta (E = 1.25 MeV, D = 105 Gy ) as well as transient CC created in the crystals under irradiation with pulsed electron beam (E = 0.25 MeV, pulse duration 10 ns, fluence 1012 cm-2, time interval of registration 0-500 ns). On the basis of the performed study of optical absorption spectra of the as-grown and irradiated crystals it was established the correlation between a defect subsystem of as-grown crystals and a type of CC induced by radiation in the crystals. The role of Ca2+ dopant ions in the processes of CC formation is examined. Models of the stable…
Radiation displacement defect formation in some complex oxide crystals
2000
The work is devoted to an analysis of the formation processes of radiation displacement defects (RDDs) and color centers (CCs) under irradiation of complex oxide crystals. The results of the displacement process simulation as well as the analysis of the RDDs and CCs accumulation kinetics in some complex oxide crystals are presented. New experimental results on additional absorption spectra induced by neutron irradiation of LiNbO3 (LNO) crystals doped with Fe and Cr and YAlO3 (YAP) crystals doped with Nd and Er as well are presented. Dose dependencies are compared and their peculiarities are discussed. ” 2000 Elsevier Science B.V. All rights reserved.
Displacement Defect Formation in Complex Oxide Crystals under Irradiation
2000
The work is devoted to an analysis of formation processes of the radiation displacement defects (RDDs) and colour centres (CCs) in complex oxide crystals under irradiation. The calculation results on: the displacement process simulation as well as an analysis of the RDD and CC accumulation kinetics are presented. New experimental results on additional absorption spectra induced by neutron irradiation of LiNbO(3) (LNO) crystals doped with Fe and Cr and YAlO(3) (YAP) crystals doped with Nd and Er as well are presented. Dose dependencies of the additional absorption are compared and their peculiarities are discussed. The obtained results confirm that CCs causing the irradiation induced absorpt…
Band Gap Engineering and Trap Depths of Intrinsic Point Defects in RAlO3 (R = Y, La, Gd, Yb, Lu) Perovskites
2021
The work was supported by the Polish National Science Centre (Project No. 2018/31/B/ST8/00774), by the NATO SPS Project G5647, and by the Ministry of Education and Science of Ukraine (Project DB/Kinetyka no. 0119U002249). L.V. acknowledges support of the National Research Foundation of Ukraine under Grant No. 2020.02/0373 “Crystalline phosphors’ engineering for biomedical applications, energy saving lighting and contactless thermometry”. Researchers from Tartu were supported by the ERDF fundings in Estonia granted to the Centre of Excellence TK141 “Advanced materials and high-technology devices for sustainable energetics, sensorics and nanoelectronics (HiTechDevices)” (Grant No. 2014-2020.4…
Luminescence Properties and Decay Kinetics of Mn2+ and Eu3+ Co-Dopant Ions In MgGa2O4 Ceramics
2018
A. Luchechko gratefully acknowledges a grant from the Institute of Physics PAS for a research visit to the institute, while A.I. Popov has been supported by project LZP-2018/1-0214 from the Latvian Council of Science.
Physical Properties of Ba0.95Pb0.05TiO3+0.1%Co2O3
2012
The single-phase perovskite structure of the Ba0.95Pb0.05TiO3+0.1%Co2O3 ceramics was confirmed by the X-ray diffraction method. Microstructural studies revealed that the samples were of good quality and chemically homogeneous. The thermal behaviour of ceramics was studied using the in situ high-temperature X-ray synchrotron powder diffraction investigation. The energy gap of about 3.2 eV was estimated using a reflectance spectroscopy. Measurements showed the influence of Pb and Co on the character of phase transition in the BaTiO3 structure. The results were compared to the ones obtained for pure BaTiO3.
Afterglow, TL and OSL properties of Mn2+-doped ZnGa2O4 phosphor
2019
The work was supported by Latvian Research Council via LZP-2018/1–0214 research project as well as the Latvian-Ukrainian Joint Research Project (LV-UA/2016/1 in Latvia and M/8-2018 (No. 0118U001672) in Ukraine), and by the NATO SfP Project G4649. The work was also partially supported by the Polish National Science Center (project 2018/31/B/ST8/00774). A. Luchechko gratefully acknowledges a grant from Institute of Physics PAS for a research visit to the Institute.