A study of the behaviour of Pt supported on CeO2–ZrO2/Al2O3–BaO as NO storage–reduction catalyst for the treatment of lean burn engine emissions
Abstract The behaviour of a Pt(1 wt.%) supported on CeO2–ZrO2(20 wt.%)/Al2O3(64 wt.%)–BaO(16 wt.%) as a novel NOx storage–reduction catalyst is studied by reactivity tests and DRIFT experiments and compared with that of Pt(1%)–BaO(15 wt.%) on alumina. The former catalyst, designed as a hydrothermally stable sample, is composed of an alumina modified with Ba ions and an overlayer of ceria-zirconia. The results pointed out that during the calcination barium ions migrates over the surface of the catalyst which thus show a good NOx storage–reduction behaviour comparable with that of Pt–BaO on alumina, although Ba ions result much better dispersed.
Surface and bulk changes of a Pt 1%/Ce0.6Zr0.4O2 catalyst during CO oxidation in the absence of O2
The reduction of a Pt 1%/Ce0.6Zr0.4O2 catalyst by CO in the absence of gaseous oxygen was studied by transient reactivity tests, temperature programmed surface reaction with CO, flow thermogravimetric tests and DRIFTS experiments, in order to obtain information generally on the OSC properties and, specifically, on the mechanism of CO oxidation over both, Pt catalyst and support-only sample (Ce0.6Zr0.4O2). The results of thermogravimetric experiments showed the presence of an induction time in the weight change % of the catalyst, depending on the CO concentration in the gas flow. This induction time could be related to the presence of two oxygen reactive sites. The first one leads to strongl…
Photoelectrochemical properties of doped lanthanum orthoferrites
Abstract LaFeO 3 powders doped with Sr (20 mol%) and Cu (0-10-20 mol%) were prepared by citrate auto-combustion synthesis and investigated in terms of crystal structure, morphology, surface area and optical properties. All powders showed photocurrent response in the form of a pasted and annealed electrode and as slurry electrode; the highest value was obtained for undoped orthoferrite calcined at 600 °C. Their physical–chemical properties were related to photoelectrochemical behaviour. The position of the quasi-Fermi level of electrons for all the photocatalysts calcined in the range 600–980 °C is about the same within experimental error (between −0.62 and −0.67 V with respect to Ag/AgCl re…