Synthesis and characterization of catalytic iridium nanoparticles in imidazolium ionic liquids
Abstract The reduction of [Ir(cod)Cl]2 (cod = 1,5-cyclooctadiene) dissolved in 1-n-butyl-3-methyl tetrafluoroborate, hexafluorophosphate and trifluoromethane sulphonate ionic liquids in the presence of 1-decene by molecular hydrogen produces Ir(0) nanoparticles. The formation of these nanoparticles follows the two-step [A → B, A + B → 2B ( k 1 , k 2 )] autocatalytic mechanism. The same mean diameter values of around 2–3 nm were estimated from in situ TEM and SAXS analyses of the Ir(0) nanoparticles dispersed in the ionic liquids and by XRD of the isolated material. XPS and EXAFS analyses clearly show the interactions of the ionic liquid with the metal surface demonstrating the formation of …
Selective Hydrogenation of 1,3-Butadiene to 1-Butene by Pd(0) Nanoparticles Embedded in Imidazolium Ionic Liquids
The reduction of Pd(acac)2 (acac=acetylacetonate), dissolved in 1-n-butyl-3-methylimidazolium hexafluorophosphate (BMI⋅PF6) or tetrafluoroborate (BMI⋅BF4) ionic liquids, by molecular hydrogen (4 atm) at 75 °C affords stable, nanoscale Pd(0) particles with sizes of 4.9±0.8 nm. Inasmuch as 1,3-butadiene is at least four times more soluble in the BMI⋅BF4 than butenes, the selective partial hydrogenation could be performed by Pd(0) nanoparticles embedded in the ionic liquid. Thus, the isolated nanoparticles promote the hydrogenation of 1,3-butadiene to butenes under solventless or multiphase conditions. Selectivities up to 97% in butenes were observed in the hydrogenation of 1,3-butadiene by Pd…
Structural properties of the quaternary Heusler alloy Co2Cr1−xFexAl
The quarternary substitutional series Co2Cr1?xFexAl was investigated by means of surface and bulk sensitive techniques in order to exploit its structural and compositional properties. Both bulk and powder samples of the alloy series were investigated to obtain specific information about this material.The long range order was determined by means of x-ray diffraction and neutron diffraction, while the site specific (short range) order was proved by extended x-ray absorption fine structure spectroscopy. The magnetic structure was investigated by M?ssbauer spectroscopy in transmission and scattering modes in order to compare and separate powder and bulk properties. The chemical composition was …