Studies of TiO<sub>2</sub> Ceramics Structure after Thermal Treatment at Different Conditions
The present work describes results of investigation of structural characteristics of TiO2 ceramics, depending on temperature and thermal treatment conditions by using a variety of characterization techniques. TiO2 ceramics was prepared by extrusion method and developed as a material for electrodes for innovative water treatment technologies. It was shown that non-stoichiometric phase TiO1.95 was observed after thermal treatment of TiO2 ceramics under high vacuum conditions.
Phase Transition in Niobophosphate Glass-Ceramic
Phase transition during crystallization of glass to glass-ceramic in system P2O5-CaO-Nb2O5-Na2O was studied. Several heating rates were compared – 1, 2, 5, 11 and 20°Cmin-1. DTA, XRD, FTIR and Raman analyses were performed. Niobophosphate glass-ceramic is found to form utterly different crystalline phases depending on maximal heating temperature, heating rate and time of maximal temperature maintenance. Crystallization temperatures of the same phases are strongly dependent on heating rate, while crystallinity of obtained phases is not. At lower temperatures poorly crystalline phosphates (Ca3(PO4)2, Ca10Na(PO4)7, Ca2P2O7) and niobates (NaNbO3 and Nb2O5) are identified. At higher temperatures…