Clara I. D. Bica
Dilute solution properties of polybutadiene modified by 4-phenyl-1,2,4-triazoline-3,5-dione
The dilute solution properties of 4-phenyl-1,2,4-triazoline-3,5-dione-modified polybutadienes were studied in tetrahydrofuran by static and dynamic light scattering and compared with those from unmodified polybutadiene chains. For the unmodified polymer, the scaling laws were established and the coil interpenetration parameter k f0 was determined in the thermodynamically good solvent tetrahydrofuran ; the chains exhibited common flexible chain behavior. For the modified polybutadiene, the results indicate at infinite dilution a weak extent of intermolecular crosslinking via the urazole groups, coupled with a very high extent of intramolecular ring formation. In order to evaluate the fractio…
Behaviour of modified and unmodified polybutadienes in the semidilute regime
Abstract The association behaviour of polybutadiene modified with 4-phenyl-l,2,4-triazoline-3,5-dione was studied in semidilute solution through static (SLS) and dynamic light scattering (DLS). The results were compared with the unmodified polybutadiene, whose behavior in semidilute solution was also studied as function of the molecular weight. At higher concentrations a small-angle excess scattering in SLS and a slow mode motion in DLS were observed both for modified and unmodified polybutadienes suggesting the presence of large clusters. Increasing the polymer concentration, the mass fraction of the slow motion increases up to values near 1, indicating a proximity to the gel point. For po…