Formation of cobalt silicide from filter metal vacuum arc deposited films
The thermal reaction of Co film deposited on Si(111) surfaces by a high current filter metal vacuum arc (FMEVAD) system has been studied. After deposition the films were annealed over the 400-900 degrees C temperature range for 30 min. Rutherford backscattering spectrometry (RBS) was used to characterize the elemental depth distributions in the films subjected to different annealing temperatures. Ordered chemical phases were determined by glancing-incidence X-ray diffraction (GIXRD) and the morphology was determined by cross section transmission electron microscopy (TEM). The results show that the phases formed are Co2Si at 400 degrees C, CoSi + Coo at 500 degrees C, CoSi + CoSi2 at 600 deg…
Formation of cobalt silicide films by ion beam deposition
Abstract Thin films of cobalt silicide are widely used as metallization in very large-scale integrated electronic circuits. In this study, Co ions were deposited on Si(1 1 1) wafers by a high beam current filter metal vacuum arc deposition (FMEVAD) system. Surface silicide films were formed after annealing from 500 to 700 °C for 30 min. The results show that a thin CoSi2 surface layer with both a smooth surface topography and sharp interface can be achieved by annealing at 700 °C. The CoSi phase and O contamination were observed in the samples that were annealed at lower temperatures.