Influence of temperature on the hydration products of low pH cements

International audience; The chemical evolution of two hydrated "low pH" binders prepared from binary (60% Portland cement + 40% silica fume) or ternary (37.5% Portland cement +32.5% silica fume + 30% fly-ash) mixtures was characterized over one year at 20 degrees C. 50 degrees C, and 80 degrees C. The main hydrates were Al-substituted C-S-H. Raising the temperature from 20 to 80 degrees C caused a lengthening and cross-linking of their silicate chains. Ettringite that formed in pastes stored at 20 degrees C was destabilized. Only traces of calcium sulfate (gypsum and/or anhydrite) reprecipitated after one year in some materials cured at 50 degrees C and 80 degrees C. The sulfates released w…