Behaviour of advanced tritium breeder pebbles under simultaneous action of accelerated electrons and high temperature
2017
The authors greatly acknowledge the technical and experimen-tal support of O. Valtenbergs and L. Avotina (Institute of Chemical Physics, University of Latvia). The work is performed in the frames of the University of Latvia financed project No. Y9-B044-ZF-N-300, “Nano, Quantum Technologies, and Innovative Materials for Eco-nomics”.
Characterisation and radiolysis of modified lithium orthosilicate pebbles with noble metal impurities
2017
Modified lithium orthosilicate (Li4SiO4) pebbles with additions of titanium dioxide (TiO2) are suggested as an alternative tritium breeding ceramic for the European solid breeder test blanket module. The noble metals – platinum (Pt), gold (Au) and rhodium (Rh), can be introduced into the modified Li4SiO4 pebbles during the melt-based process, due to the corrosion of Pt-Rh and Pt-Au alloy crucible components. In this study, the surface microstructure, chemical and phase composition of the modified Li4SiO4 pebbles with different contents of the noble metals was analysed. The influence of the noble metals on the radiolysis was evaluated after irradiation with accelerated electrons (E = 5 MeV),…
Formation and accumulation of radiation-induced defects and radiolysis products in modified lithium orthosilicate pebbles with additions of titanium …
2016
Abstract Lithium orthosilicate (Li4SiO4) pebbles with 2.5 wt.% excess of silicon dioxide (SiO2) are the European Union's designated reference tritium breeding ceramics for the Helium Cooled Pebble Bed (HCPB) Test Blanket Module (TBM). However, the latest irradiation experiments showed that the reference Li4SiO4 pebbles may crack and form fragments under operation conditions as expected in the HCPB TBM. Therefore, it has been suggested to change the chemical composition of the reference Li4SiO4 pebbles and to add titanium dioxide (TiO2), to obtain lithium metatitanate (Li2TiO3) as a second phase. The aim of this research was to investigate the formation and accumulation of radiation-induced …
Overview of the HCPB Research Activities in EUROfusion
2018
In the framework of the EUROfusion’s Power Plant Physics and Technology, the working package breeding blanket (BB) aims at investigating four different BB concepts for an EU demonstration fusion reactor (DEMO). One of these concepts is the helium-cooled pebble bed (HCPB) BB, which is based on the use of pebble beds of lithiated ternary compounds and Be or beryllides as tritium breeder and multiplier materials, respectively, EUROFER97 as structural steel and He as coolant. This paper aims at giving an overview of the EU HCPB BB Research and Development (R&D) being developed at KIT, in collaboration with Wigner-RCP, BUTE-INT, and CIEMAT. The paper gives an outline of the HCPB BB design evolut…
X-ray induced defects in advanced lithium orthosilicate pebbles with additions of lithium metatitanate
2019
Abstract Advanced lithium orthosilicate (Li4SiO4) pebbles with additions of lithium metatitanate (Li2TiO3) as a secondary phase have attracted international attention as an alternative solid-state candidate for the tritium breeding in future nuclear fusion reactors. In this research, the generation of radiation-induced defects in the Li4SiO4 pebbles with various contents of Li2TiO3 was analysed in-situ by X-ray induced luminescence technique. After irradiation with X-rays, the accumulated radiation-induced defects in the Li4SiO4 pebbles were studied by electron spin resonance, thermally stimulated luminescence and absorption spectrometry. On the basis of the obtained results, it is conclude…