Photo-electrochemical investigation of anodic oxide films on cast Ti–Mo alloys. I. Anodic behaviour and effect of alloy composition
Abstract The anodic behaviour of cast Ti–Mo alloys, having different Mo contents (6–20 wt.%), was investigated in acidic and neutral aerated aqueous solutions. All sample showed a valve-metal behaviour, owing to formation and thickening of barrier-type anodic oxides displaying interference colours. Growth kinetics of passive films is influenced by both anodizing electrolyte and composition of the starting alloy. This last parameter was found to change also the solid-state properties of the films, explored by photoelectrochemical and impedance spectroscopy experiments. Thicker films ( U f = 8 V/MSE) grown on alloys richer in Mo showed more resistive character and a photocurrent sign inversi…
The effect of thickness on the composition of passive films on a Ti–50Zr at% alloy
Abstract Anodic films were grown potentiodynamically in different electrolytes (pH = 1–14) on a Ti–50Zr at% cast alloy, obtained by fusion in a voltaic arc under argon atmosphere. The thickness of the films was varied by changing formation potential from the open circuit potential up to about 9 V; growth was followed by 30 min stabilization at the forming potential. Films having different thicknesses were characterized by photocurrent spectroscopy (PCS) and electrochemical impedance spectroscopy (EIS). Moreover, film composition was analyzed by X-ray photoelectron spectroscopy (XPS). Regardless of the anodizing conditions, passive films on the Ti–50Zr at% alloy consist of a single layer mix…
Photo-electrochemical and impedance investigation of passive layers grown anodically on titanium alloys
Abstract The anodic behaviour of two titanium cast alloys, obtained by fusion in a voltaic arc under argon atmosphere, was analyzed in aerated aqueous solutions having different pH values. In all solutions the alloys, having nominal compositions Ti–50Zr at.% and Ti–13Zr–13Nb wt.%, displayed a valve-metal behaviour, owing to the formation of barrier-type oxide films. Passive films, grown potentiodynamically up to about 9 V, were investigated by photocurrent spectroscopy (PCS) and electrochemical impedance spectroscopy (EIS). These passive layers show photoactivity under anodic polarizations, with optical gaps close to 3.55 and 3.25 eV for the binary and the ternary alloy, respectively, indep…