0000000000347392
AUTHOR
S. Król
Frictional behaviour of oxygen diffusion hardened titanium in dry sliding against Co–28Cr–5W–4Fe–3Ni–1Si cobalt alloy
Abstract The results of conformal pin-on-disc tribological tests of a hard layer of the solid solution of oxygen in α-titanium sliding against a Co–28Cr–5W–4Fe–3Ni–1Si cobalt alloy counterspecimen are presented. The α-Ti(O) layer was diffusely produced over 2–8 h of oxidising in the superficial zone of a technical quality titanium specimen. The friction and wear responses of the system were recorded and the wear mechanisms were studied. Investigations of the material structure and chemical constitution in micro-areas of the titanium specimen, cobalt alloy counterspecimen and wear debris formed in dry sliding were performed with a Philips XL20 microscope equipped with an EDAX analyser. Crush…
Friction and wear properties of titanium and oxidised titanium in dry sliding against hardened C45 steel
Abstract The aim of the paper is to present the results of conformal pin-on-disc tribological tests concerning the hard oxidised zone created in superficial layer of a titanium specimen sliding against the hardened to a hardness of 690 HV carbon C45 steel counterspecimen. Tribological testing was carried out at room temperature and at unlubricated conditions. After tests the structures and chemical compositions of the wear debris and worn surfaces were a subject of SEM and X-ray investigations. In comparison with the baseline the technical quality titanium/C45 steel couple, the wear and lifetime performance of the oxidised titanium/steel C45couple was markedly superior. Dominant wear debris…
Comparison of the friction and wear properties of titanium and oxidised titanium in dry sliding against sintered high speed steel HS18-0-1 and against C45 carbon steel
Abstract The paper presents the results of conformal pin-on-disc tribological tests concerning the hard oxidised zone, α-Ti(O), created at the surface of a titanium specimens sliding against the sintered and hardened up to 850 HV30, Grade T1 high speed steel (HS18-0-1) counterspecimens. Comparison with the results obtained for the tests performed against hardened up to 620 HV30 C45 carbon steel counterspecimens has been done. Testing was carried out at room temperature and at unlubricated conditions. After tests the structures and compositions of the worn surfaces and wear debris were a subject of LOM, SEM observations and X-ray microanalyses. In comparison with the baseline—the Ti/T1 HSS c…
Investigations on friction and wear mechanisms of the PVD-TiAlN coated carbide in dry sliding against steels and cast iron
Abstract The tribological behaviour of the monolayer PVD-titanium aluminium nitride (TiAlN) coated carbide inserts in unidirectional dry sliding against steel and cast iron counterparts was investigated using the pin-on-disc standard test with varying sliding speeds and normal loads. Three different materials of various machinability rates were used as the counterparts, namely the normalised medium carbon steel C45 equivalent to AISI 1045, austenitic stainless steel 1H18N9T equivalent to AISI 304 and gray cast iron EN-GJL-300 with flake-shaped graphite. A pin-on-disc device with round tool inserts was used to conduct friction and wear tests in which both the friction coefficient and the lin…