I. Alencar
Irradiation effects in CaF2probed by Raman scattering
The formation conditions and dynamics of Ca colloids and point defects that appear in irradiated single crystals of CaF2 were investigated by Raman spectroscopy. The intensity changes in the Raman spectra because of the presence of different concentrations of point defects and Ca colloids that emerged in CaF2 after irradiation with 2.2 GeV Au ions were used to study their distribution and stability under illumination with three laser wavelengths (473, 532 and 633 nm) at different output powers (2 to 200 mW). A damage saturation at a fluence of 6 × 1011 ion cm−2 was observed. The dependence of the spectral changes on the ion fluence can be described by a core/halo damage cross-section model.…
Reversible Tuning of Ca Nanoparticles Embedded in a Superionic CaF2 Matrix
Controlling the size and shape of metallic colloids is crucial for a number of nanotechnological applications ranging from medical diagnosis to electronics. Yet, achieving tunability of morphological changes at the nanoscale is technically difficult and the structural modifications made on nanoparticles generally are irreversible. Here, we present a simple nonchemical method for controlling the size of metallic colloids in a reversible manner. Our strategy consists of applying hydrostatic pressure on a Ca cationic sublattice embedded in the irradiated matrix of CaF2 containing a large concentration of defects. Application of our method to CaF2 along with in situ optical absorption of the Ca…