Blue lasing at room temperature in high quality factor GaN/AlInN microdisks with InGaN quantum wells
The authors report on the achievement of optically pumped III-V nitride blue microdisk lasers operating at room temperature. Controlled wet chemical etching of an AlInN interlayer lattice matched to GaN allows forming inverted cone pedestals. Whispering gallery modes are observed in the photoluminescence spectra of InGaN/GaN quantum wells embedded in the GaN microdisks. Typical quality factors of several thousands are found (Q>4000). Laser action at similar to 420 nm is achieved under pulsed excitation at room temperature for a peak power density of 400 kW/cm(2). The lasing emission linewidth is down to 0.033 nm.
Current status of AlInN layers lattice-matched to GaN for photonics and electronics
We report on the current properties of Al1-x InxN (x approximate to 0.18) layers lattice- matched ( LM) to GaN and their specific use to realize nearly strain- free structures for photonic and electronic applications. Following a literature survey of the general properties of AlInN layers, structural and optical properties of thin state- of- the- art AlInN layers LM to GaN are described showing that despite improved structural properties these layers are still characterized by a typical background donor concentration of ( 1 - 5) x 10(18) cm(-3) and a large Stokes shift (similar to 800 meV) between luminescence and absorption edge. The use of these AlInN layers LM to GaN is then exemplified …