On the formation of lamellae during annealing of extended chain crystals of radiation-polymerized trioxane

Abstract The structure changes of radiation-polymerized trioxane taking place during annealing have been studied by means of electron microscopy, X-ray small- and wide-angle scattering, and differential thermal analysis. The original fibrillar crystals, supposedly consisting of extended chains, change into lamellar crystals due to annealing at temperatures between 150° and 190°C. Lamella formation can be connected with the appearance of a long period of about 200A which is not observed in the unannealed sample. During annealing within the same temperature range the X-ray reflections due to the twin structure of the original polytrioxane disappear, whereas the orientation of the fraction wit…

Schmelz- und Rekristallisationsvorgänge bei Polyäthylen-Einkristallen

Die aus verdunnten Losungen hergestellten Einkristalle des Polyathylens waren bereits der Gegenstand zahlreicher Untersuchungen (1), da die Struktur dieser Kristalle von grundsatzlicher Bedeutung fur die Diskussion aller physikalischen Eigenschaften der teilkristallinen Hochpolymeren ist. Insbesondere wurde auch die Frage nach dem Kristallisationsgrad α der sogenannten Einkristalle schon haufig erortert. Diese Grose wurde mit Hilfe verschiedener Methoden in mehreren Laboratorien gemessen, und in der uberwiegenden Mehrzahl der Falle wurde festgestellt, das die Polyathylen-Einkristalle je nach den Kristallisationsbedingungen einen Anteil von 10–20% an nichtkristallisierten kettensequenzen ent…

Untersuchungen zum Schmelzverhalten des verstreckten Polyäthylens mit Hilfe der Differential-Thermo-Analyse

On the reliability of the gradient column method for measuring densities of polymer single crystals