Islands of Immiscibility for Solutions of Compatible Polymers in a Common Solvent: Experiment and Theory
Experimentally obtained islands of immiscibility are reported for the systems PS/PVME/THF at 20 °C and for PS/PVME/CH at 55 °C (PS: polystyrene, PVME: poly(vinyl methyl ether), THF: tetrahydrofuran, CH: cyclohexane). THF is a good solvent and CH is a marginal solvent for both polymers. In the case of THF, information on the Flory−Huggins interaction parameters of the three binary subsystems suffices for a qualitative prediction of the phase behavior of the ternary system. Quantitative agreement can be achieved by means of composition-independent ternary interaction parameters. For the marginal solvent CH, the exclusive use of binary interaction parameters wrongly predicts complete miscibili…
Consequences of linking charged and uncharged monomers to binary copolymers studied in dilute solution. Part I: Viscometric behavior of the homopolymers, the effects of charging, and uncommon salt effects
Abstract Intrinsic viscosities, generalized intrinsic viscosities and viscometric interaction parameters were measured for aqueous solutions of poly(ethylene oxide) [PEO], poly(N,N-dimethyl aminoethyl methacrylate) [PR] (uncharged) and for poly{[2-(methacryloyloxy)ethyl] trimethylammonium iodide} [PR+] (charged) within a wide range of molar masses. In this manner it was possible to establish the information required for the study of non-additivity effects upon the formation of binary copolymers from the monomers specified above. The following additional items were of particular interest: The effects of charging PR to PR+ and the composition dependence of the coil overlap in the case of sali…