SYNTHESIS AND CHARACTERIZATION OF SB-SUBSTITUTED (K0.5Na0.5)NbO3 PIEZOELECTRIC CERAMICS
ABSTRACT Lead-free piezoelectric ceramics (K0.5Na0.5)(Nb1-xSbx)O3+0.5 mol.%MnO2, where x = 0 ÷ 0.10, with single phase structure and rhombohedral symmetry at room temperature were prepared by conventional ceramic technology. The optimal sintering temperatures of compositions were within 1100°–1140°C. MnO2 functions as a sintering aid and effectively improves the densification. The samples reached density from 4.26 g/cm3 for undoped (K0.5Na0.5)NbO3 to 4.40 g/cm3 for Mn/Sb5+ co-doped ceramics. The co-effects of MnO2 doping and Sb5+ substitution lead to significant improvement in dielectric and piezoelectric properties: e at the Tc increased from 6000 (KNN) to 12400 (x = 0.04), d33 = 92 ÷ 192 …
INFLUENCE OF MONOXIDES ADDITION ON SINTERING OF SODIUM-POTASSIUM NIOBATES SOLID SOLUTION
ABSTRACT In this paper the preparation, structure and dielectric parameters of ceramics from different powders of pure potassium sodium niobate (KNN) and KNN doped with 1.0 wt% of Li2O, CdO, Bi2O3, MnO2, V2O5 and WO3 have been studied. The dopping of sintering aids did not affect the crystallographic structure of the ceramics significantly; all ceramic samples had a single-phase perovskite structure. Added elements Li2O, CdO, MnO2, V2O5 effectively decreased the sintering temperature of KNN (50°–80°C). All sintering aids influenced sinterability, microstructure and dielectric properties of ceramics. Dielectric constant for doped samples increased from 6000 up to 8000.
SINTERING OF LEAD-FREE (K0.5Na0.5)NbO3 BASED SOLID SOLUTION
ABSTRACT In this study lead-free solid solution (K0.5Na0.5)NbO3 was prepared, structure, dielectric parameters of ceramics were investigated. The doping of sintering aids did not affect the crystallographic structure of the ceramics significantly; all ceramic samples had a single-phase perovskite structure. Added elements CdO, ZnO, MnO2, V2O5 effectively decreased the sintering temperature of KNN by 50°–80°C. All sintering aids influenced sinterability, microstructure and dielectric properties of ceramics. Dielectric constant for doped samples increased from 6000 up to 8000; Pr = 15 μC/cm2, Ec = 9 kV/cm, d33 = 110 pC/N, kp = 0.38 and Qm = 190 for MnO2 doped samples.