Chemical effect on the XPS spectra of the valence band and on O KLL and Pd MNN Auger spectra in pumice-supported catalysts
X-ray photoelectron spectra of the valence band and X-ray-excited O KLL Auger transition of pumice-supported Pd and Pt catalysts have been obtained and compared to the corresponding spectra of pumice (a naturally occurring amorphous aluminosilicate). The changes observed indicate interaction between metal and support. The valence region of the catalysts consists of three large peaks: one due to the d band of the metals and the other to the O 2p non-bonding orbitals and bonding-type orbitals formed by a mixing of the atomic orbitals (O 2p, Si 3s and Si 3p) of oxygen and silicon from the support. The intensity decrease of the component due to the bonding orbitals, observed in the catalyst spe…
The structure of pumice: An XPS and27Al MAS NMR study
In order to investigate the surface structure of pumice, an amorphous aluminosilicate, samples of pumice and of standards of silica and alumina have been studied by x-ray photoelectron spectroscopy (XPS). The effect of a mild acid leaching was also considered. The analysis of the Si 2p, Al 2p and O 1s photoelectron peaks and the Si KLL and O KLL Auger peaks indicated that pumice is formed by tetrahedral silica with some units being replaced by aluminate, AlO2−. The acid treatment decreases the alkali and the aluminate ions. X-ray photoelectron spectra of the valence band of pumices and of standards of Al2O3 and SiO2 agree with the core-level results. To support the conclusions from the XPS …
Two-Length-Scale Structure in Some Computer-Generated Aggregates Grown by Diffusion-Limited Aggregation
AbstractThe properties of some aggregates “grown” on a computer by diffusion-limited aggregation have been investigated. Calculations showed that the intensity of the small-angle x-ray and neutron scattering from the aggregates was proportional to q−D for qL ≫ 1, where D > 0, L is a length that characterizes the large-scale structure of the aggregate, q = 4πλ−1 sin(θ/2), γ is the wavelength, and θ is the scattering angle. The magnitude of the exponent D was appreciably smaller than the fractal dimensions that many simulations have shown to be typical of the mass fractal aggregates grown by diffusion-limited aggregation. The calculations suggest that the aggregates have structure on two d…
XPS study of pumice-supported palladium and platinum catalysts
An XPS study has been performed on samples of monometallic of palladium and platinum and on bimetallic Pd-Pt catalysts supported on pumice. A negative shift of about 0.5 eV in the Pd 3d and Pt 4f binding energies of the catalysis relative to the energies of the same levels in the pure metals suggested an increase in the electron density in both metals. A quantitative XPS analysis indicated that the supported metals did not modify the surface atomic composition of pumice