Co-precipitation of Mg-doped Ni0.8Co0.1Mn0.1(OH)₂:effect of magnesium doping and washing on the battery cell performance
Co-precipitation of Ni0.8Co0.1Mn0.1(OH)2 (NCM811) and Mg-doped (0.25 wt% and 0.5 wt%) NCM811 precursors is carried out from concentrated metal sulphate solutions. In this paper, the aim is to study the role of magnesium dopant in the co-precipitation step of NCM811, the cathode active material and further the Li-ion battery cell performance. Based on the results, magnesium was fully co-precipitated in the NCM811 precursors, as expected from thermodynamic calculations. The presence of magnesium in these precursors was also confirmed by several characterization methods and magnesium was evenly distributed in the sample. It was observed that tapped density decreased and surface area increased …
Water leaching of roasted vanadium slag : Desiliconization and precipitation of ammonium vanadate from vanadium solution
This research investigated water leaching of roasted vanadium slag and studied the effects of leaching parameters, such as agitation speed, temperature, liquid-to-solid ratio, and leaching time. Further, solution purification via desiliconization and precipitation of ammonium vanadate were studied using the vanadium solution obtained from the water leaching of roasted vanadium slag. Vanadium solution contains residual silicon (1.67 g/L), which should be removed before ammonium vanadate precipitation. Based on the results, vanadium can be effectively recovered from vanadium slag and a recovery efficiency of 96.9% was obtained under optimal water leaching conditions. During solution purificat…
Precipitation of potassium as hazenite from washing water of spent alkaline batteries
Hazenite (KNaMg2(PO4)2 × 14 H2O), a new type of struvite mineral, was precipitated from the potassium-rich washing water of spent alkaline battery black mass. Hazenite can be used as a fertilizer, which would be an additional benefit derived from the sustainable recovery of battery materials. Precipitation experiments were performed using different pH values (9.5–12), Mg:K:PO4 ratios ((1.0–1.5):1:(1.0–1.5)) and temperatures (10–40 °C). Based on the results, hazenite precipitated in a wide pH range under alkaline conditions. The precipitation kinetics were fast, and the purity of the hazenite was high. Overall, hazenite can be precipitated at room temperature without the addition of excess c…
Leaching characteristics of Sc-enriched, Fe-depleted acidic slags
Scandium is currently classified as a critical raw material for the European Union, and several research projects focus on the search for new sources to supply to its expected increasing demand. The Kiviniemi mafic intrusion in Finland is a potential primary source for Sc; at Kiviniemi, Sc occurs mainly within the lattices of ferrous silicates, clinopyroxene and amphibole. Some of the main challenges in leaching of Kiviniemi-type feed material are related to either the complexity of Fe and Ti separation from Sc-containing solutions or a possible gelation problem when leaching a material with a high SiO2 content. According to preliminary beneficiation tests, direct acid leaching of the Kivin…
Effect of Reaction Conditions on the Coprecipitation of Ni(OH)2 for Lithium-Ion Batteries
Electrochemical performance of cathode active materials (CAMs) is dependent on the properties of coprecipitated precursors (pCAMs). This is a sensitive process affected by several reaction parameters such as temperature, pH, concentration of reactants, agitation rate, and residence time. In this paper, the effect of parameters influencing the particle size growth and the physical properties, such as particle morphology and tapped density, was studied in the coprecipitation of Ni(OH)2. Formation of a homogeneous population with narrow particle size distribution was observed, followed by a more heterogeneous population of dense particles. Ammonia concentration and residence time had significa…