Optical, infrared and electron-microscopy studies of metallic clusters in layered crystals
Abstract An influence of ( Cd i ) n metallic clusters on the optical absorption and phonon spectra of CdI 2 crystals was studied. Metallic clusters of spherical shape were formed during the growth of non-stoichiometric crystals. Radii of clusters are in range from 10 to 500 nm according to scanning electron microscopy (SEM) data. The density of clusters was estimated from fractal dimension calculations. The fractal dimension of ( Cd i ) n clusters has been found to be varied from 1.488 to 1.793. In the framework of Mie theory the spectral and size dependencies of extinction coefficients were calculated. From the experimentally obtained spectra it is evident that the metallic clusters are re…
Long-term evolution of luminescent properties in CdI2 crystals
Fresh and aged melt-grown or gas-phase grown CdI2 crystals are studied by means of low-temperature photoluminescence spectroscopy. Noticeable transformations of emission spectra are observed after long-term aging. The formation of nanostructures containing cadmium oxide and cadmium hydroxide as well as the changes in local surrounding of iodine atoms and the possible growth of polytypic modifications of CdI2 are taken into account when considering the diversity of optical spectra.
BiI3 nanoclusters in melt-grown CdI2 crystals studied by optical absorption spectroscopy
Optical absorption spectroscopy of CdI2–BiI3 layered crystals has been performed in the temperature range of 77–300 K. The main absorption, observed in these crystals at 2.59 eV is related to quantum confined exciton absorption of bimolecular BiI3 cluster. Low energy absorption peaks at 2.38 eV, 2.06 eV and 1.94 eV can be tentatively assigned to larger clusters composed of 4, 6 or more BiI3 molecules. In ultra-thin samples of CdI2–BiI3 several bands at 2.84 eV, 3.03 eV and 3.27 eV were observed which are ascribed to higher excited states of the excitons in bimolecular BiI3 cluster.