Kazuo Gesi
Ferroelectricity in {N(CH3)4}2ZnI4
Dielectric properties of the {N(CH 3 ) 4 } 2 ZnI 4 crystal were studied between room temperature and 4.2 K. Two phase transitions were seen from dielectric constant anomalies at T 1 =254 K and T c =210 K on cooling. Ferroelectric hysteresis loops were observed along the c -direction below T c with a low frequency applied field of 0.0025 Hz. The spontaneous polarization obtained by pyroelectric charge measurement tended to be 2.5×10 -3 C/m 2 at 0 K.
Effect of Hydrostatic Pressure on the Phase Transitions of {N(CH3)4}2ZnCl4-xBrxMixed Crystals
Single crystals of the solid solution system {N(CH 3 ) 4 } 2 ZnCl 4- x Br x have been prepared in a low x region, and the effect of hydrostatic pressure on the phase transitions were measured for x =0.2 and 0.3. The normal-to-incommensurate phase transition temperatures increase linearly with increasing pressure with the rates of 0.126 K/MPa and 0.129 K/MPa for x =0.2 and 0.3 crystals, respectively. The ferroelectric III phase disappears at about 60 MPa for x =0.2 crystal. On the other hand, phase III is not observed for the x =0.3 crystal both at 0 pressure and at high pressures. The II-IV or III-IV transition temperatures also increases with increasing pressure with the rates of 0.162 K/M…