Organic/inorganic molecular conductors based upon perylene and Lindquist-type polyoxometalates

The preparation, structures and physical properties of the organic/inorganic radical salts based upon perylene (per) and Lindquist type polyoxometalates (POMs) are reported. Three new hybrid salts have been prepared: (per)5[Mo6O19] (1), (per)5[W6O19] (2), and (per)5[VW5O19] (3). Only structures 1 (P, Z = 2) and 3 (P, Z = 2) were fully determined as compound 2 was found to have unit cell parameters practically identical to 1 and, therefore, is considered isostructural with the latter. The structures consist of interpenetrated organic and mixed organic/inorganic layers in the ac plane alternating along the a direction. The organic layers present a novel packing mode of the perylene molecules …

New conducting radical salts based upon Keggin-type polyoxometalates and perylene

Three new radical salts, Per6[PMo12O40]·CH2Cl2 (1), Per6[PMo12O40]·CH3CN (2), and Per9(NBu4)4[SiW12O40]2 (3) (Per = perylene), have been synthesised and their electrical and magnetic properties characterised. These three salts are diamagnetic and they behave as semiconductors with room temperature conductivities of 69, 3.6 and 0.85 S cm−1. While salt 2 presents hole-type conduction and 3 exhibits electron-dominated electrical transport properties, salt 1 shows at 150 K an abrupt change in the thermal dependence of the electrical conductivity and the Seebeck coefficient suggesting a phase transition.

Metallic Conductivity in a Polyoxovanadate Radical Salt of Bis(ethylenedithio)tetrathiafulvalene (BEDT-TTF): Synthesis, Structure, and Physical Characterization ofβ″-(BEDT-TTF)5[H3V10O28]·4H2O