SPS-assisted preparation of the Magnéli phase WO2.90 for thermoelectric applications
We describe the preparation and simultaneous consolidation of WO2.90 by spark plasma sintering (SPS). SPS allows for the direct manufacturing of large amounts of consolidated material. Synchrotron powder X-ray diffraction indicates that the material is single phase. Microstructure analysis indicates that the pellet is fully dense, allowing high-temperature thermoelectric properties to be reliably measured. The as-prepared samples of WO2.90 reach a ZT of 0.1 at 1100 K.
Enhanced thermoelectric properties of the n-type Magnéli phase WO2.90: reduced thermal conductivity through microstructure engineering
The thermoelectric properties of the Magneli phase WO2.90 were investigated, with special attention to how the thermoelectric performance can be altered by changing its microstructure. Spark plasma sintering (SPS) allowed the direct preparation of large amounts of consolidated material. Adding Ta2O5 to the reaction mixture lead to the formation of solid solutions W1−xTaxO2.90via a concurrent reaction between WO3 and Ta2O5 during the SPS treatment. In addition, micron-sized inclusions containing tungsten surrounded by WOx embedded in a WO2.90 matrix were formed, which act as additional scattering centers. As a result, the thermal conductivity of the Ta-containing samples was reduced by ≈30% …