Doping induced stable room temperature dual emission from gadolinium doped vacancy ordered double halide perovskite, Gd:Cs2SnCl6

The recent advancement in bandgap engineering through controlled doping has widen the prospectof vacancy ordered double halide perovskites (VO DHPs) by conferring them with designableoptoelectronic properties. Here, we report synthesis of Gd doped Cs2SnCl6 via a simplesolvothermal method. Gd3+ ions doping lowers the band gap from 3.8 eV to 2.8 eV and facilitatesstable room temperature dual PL emission centered at 440 nm and 610 nm. The macroscopicemission process is well supported by the confocal PL emission studies on isolated crystallites.Both the pristine (Cs2SnCl6) and Gd:Cs2SnCl6 exhibit crystalline cubic structure with Fm3m spacegroup. Rietveld refinement correlates well with the cubi…