Exchange stiffness in the Co2FeSi Heusler compound
Using Brillouin light scattering spectroscopy, we determine the spin-wave exchange stiffness D and the exchange constant A for thin films of the full Heusler compound Co2FeSi prepared by pulsed laser deposition. The thermal spin-wave spectra were measured in various magnetic fields, for different transferred spin-wave momenta, and for different film thicknesses. Fitting the observed spin-wave frequencies, we find an extraordinarily large value of
Brillouin light scattering study of Co$_{2}$Cr$_{0.6}$Fe$_{0.4}$Al and Co$_{2}$FeAl Heusler compounds
The thermal magnonic spectra of Co$_{2}$Cr$_{0.6}$Fe$_{0.4}$Al (CCFA) and Co$_2$FeAl were investigated using Brillouin light scattering spectroscopy (BLS). For CCFA, the exchange constant A (exchange stiffness D) is found to be 0.48 $\mu$erg/cm (203 meV A$^2$), while for Co$_2$FeAl the corresponding values of 1.55 $\mu$erg/cm (370 meV A$^2$) were found. The observed asymmetry in the BLS spectra between the Stokes and anti-Stokes frequencies was assigned to an interplay between the asymmetrical profiles of hybridized Damon-Esbach and perpendicular standing spin-wave modes, combined with the optical sensitivity of the BLS signal to the upper side of the CCFA or Co$_2$FeAl film.