Viscosity-molecular weight relationship for cellulose solutions in either NMMO monohydrate or cuen
The intrinsic viscosities, [η], of nine cellulose samples, with molar masses from 50 × 103 to 1 390 × 103 were determined in the solvents NMMO*H2O (N-methyl morpholin N-oxide hydrate) at 80°C and in cuen (copper II-ethlenediamine) at 25°C. The evaluation of these results with respect to the Kuhn–Mark–Houwink relations shows that the data for NMMO*H2O fall on the usual straight line in the double logarithmic plots only for M ≤ 158 103; the corresponding [η]/M relation reads log ([η]/mL g−1) = –1.465 + 0.735 log M. Beyond that molar mass [η] remains almost constant up to M ≈ 106 and increases again thereafter. In contrast to NMMO*H2O the cellulose solutions in cuen behave normal and the Kuhn–…
Effects of integrating a bioethanol production process to a kraft pulp mill
Abstract The integration of an ethanol production process based on prehydrolysis of softwood chips to a kraft pulp mill is discussed. A simulation model of this biorefinery has been created with WinGEMS simulation software to calculate the mass and energy balances of the biorefinery and to examine the effects of the integration on the operation of the pulp mill. Integrating the prehydrolysis process to the modeled pulp mill producing 1000 Adt/day of pine pulp would increase the wood consumption by 16%. With the increased wood consumption, 40 t/day of ethanol could be produced, and the excess power production could be increased by 460 MWh/day. The integration of the ethanol production proces…
Carboxymethylation of alkali extracted xylan for preparation of bio-based packaging films
This study describes the synthesis of carboxymethylxylan (CMX) and investigates its suitability as a film for packaging applications. High-purity polymeric xylan was extracted from commercial bleached birch kraft pulp and converted to CMX with three different degrees of substitution (DSs). The water vapor sorption, mechanical, and barrier properties of the films prepared from CMX were tested. Increasing DS of CMX films resulted in an increase in elongation at break and a decrease in tensile strength and Young's modulus. The DS also affected the barrier properties of the films. CMX films with higher DS showed improved (reduced) oxygen permeability (OP), and the water vapor permeability (WVP)…