Diamond nucleation on iridium: local variations of structure and density within the BEN layer
Abstract The diamond nuclei generated by the bias enhanced nucleation (BEN) on iridium are gathered in well defined areas (“domains”). In atomic force microscopy (AFM) measurements they become manifest in a 1 nm downward step. The fine structure of the carbon layer inside and outside these domains has been studied by small spot Auger electron spectroscopy (AES), high resolution transmission electron microscopy (HRTEM), AFM and lateral force microscopy (LFM). The Auger spectra of the carbon KLL peak taken in an ultra high vacuum setup revealed diamond features inside and more graphitic features outside the domains. The comparison with the intensity of the Auger signal originating from the un…
Macroscopic persistent currents in laser deposited YBa2Cu3O7 films
We have investigated persistent currents in a superconducting YBa2Cu3O7 ring of about 1 cm diameter, which was deposited as c-axis textured film on a SrTiO3 substrate by laser ablation. The currents were registered, via their magnetic field distribution, with a small vibrating pick-up coil. At 77 K persistent currents with negligible decay over 103 s have been observed below a critical current density jc=0.9×105 A/cm2, both for a field-cooled and a zero-field-cooled sample. This demonstrates that it is possible to fabricate dissipationless devices of such films on a relatively large scale.
Macroscopic persistent currents in laser ablated YBa2Cu3O7-x films
AbstractThin films of YBa2Cu3O7-x have been produced in situ by laser ablation. As the condensation of the superconducting film is done onto hot substrates (600 - 780°C) at high oxygen pressures (~ 1 mbar), this techniques does not require any special postannealing step. Thus the total process time amounts to less than 10 min. Films were found to be polycrystalline with the c-axis preferentially oriented normal to the substrate plane on single crystalline (001) SrTiO3 and (random) ZrO2, as measured by ion channeling (Xmin = 5.5 % on SrTiO3), x-ray scattering and TEM. Complete superconducting transitions above 90 K with transition widths of about 1 K have been observed even on YSZ substrates…