Slurries Introduction in Flow Injection Atomic Absorption Spectroscopic Analysis of Sewage Sludges
Abstract The direct introduction of slurries in flow Injection-flame atomic absorption spectroscopy has been studied using a single-channel manifold. The influence of flow Injection parameters on the sensitivity and accuracy of this procedure has been established. A method has been developed for the determination of copper, manganese, and lead In sewage sludge where batch digestion of the samples In a microwave oven is carried out before dilution. Both sensitivity and limit of detection of the flow Injection analysis procedure are adequate for the analysis of actual samples (the limit of detection was 0.06, 0.05, and 0.3 ppm for copper, manganese, and lead, respectively). The accuracy of th…
Direct FIA—AS determination of potassium and magnesium in cement samples by use of the slurries approach
A direct procedure has been developed for the flame atomic determination of potassium and magnesium in cement samples. A 50-mg sample is dispersed in 25 ml of 0.13M nitric acid; 100 mul of this slurry is injected in a double channel FIA manifold simultaneously with 100 mul of a 10% (w/v) lanthanum solution. This procedure allows the rapid extraction of potassium and magnesium by leaching of the sample; nitric acid is not necessary if only potassium must be determined and the sample can be diluted with only distilled water. Aqueous standards are used. The manifold employed includes a well-stirred mixing chamber, which provides an adequate on-line dilution of the sample, in order to obtain em…
Flow injection flame atomic absorption analysis of Fe and Mn in cement samples
A new procedure has been developed for the determination of Fe and Mn in cements. It consists in dispersing 50 mg of the solid sample in 25 ml of 0.15 mol/l HNO3 and 0.12 mol/l HCl solution. Acid slurries are heated at 50°C for 10 min and then different volumes of the slurry are injected into a water carrier stream. This previous acid treatment leaches the elements to be determined and permits the use of acid solutions as standards. For the Mn determination, the use of a single line flow injection manifold provides a limit of detection of 0.03 mgl−1 and a dynamic range up to 6 mgl−1. For the determination of Fe, the on-line dispersion of samples, using a well stirred mixing chamber, increas…